Source author record

Petr S. Sokolov

Petr S. Sokolov appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci

Catalog footprint

What is connected

9works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2021arXiv

Heat capacities of nanostructured wurtzite and rock salt ZnO: challenges of ZnO nano-phase diagram

Low-temperature heat capacities (Cp) of nanostructured rock salt (rs-ZnO) and wurtzite (w-ZnO) polymorphs of zinc oxide were measured in the 2-315 K temperature range. No significant influence of nanostructuring on Cp of w-ZnO has been observed. The measured Cp of rock salt ZnO is lower than that of wurtzite ZnO below 100 K and is higher above this temperature. Using available thermodynamic data, we established that the equilibrium pressure between nanocrystalline w-ZnO and rs-ZnO is close to 4.6 GPa at 300 K (half as much as the onset pressure of direct phase transformation) and slightly changes with temperature up to 1000 K.

preprint2016arXiv

Melting of B12P2 boron subphosphide under pressure

Melting of boron subphosphide (B12P2) to 26 GPa has been studied by in situ synchrotron X-ray powder diffraction in a laser-heated diamond anvil cell, and by quenching and electrical resistance measurements in a toroid-type high-pressure apparatus. B12P2 melts congruently, and the melting curve has a positive slope of 23(6) K/GPa. No solid-state phase transition was observed up to the melting in the whole pressure range under study.

preprint2015arXiv

Phonon study of rhombohedral BS under high pressure

Raman spectra of rhombohedral boron monosulfide (r-BS) were measured under pressures up to 34 GPa at room temperature. No pressure-induced structural phase transition was observed, while strong pressure shift of Raman bands towards higher wavenumbers has been revealed. IR spectroscopy as a complementary technique has been used in order to completely describe the phonon modes of r-BS. All experimentally observed bands have been compared with theoretically calculated ones and modes assignment has been performed. r-BS enriched by 10B isotope was synthesized, and the effect of boron isotopic substitution on Raman spectra was observed and analyzed.

preprint2014arXiv

Self-propagating high-temperature synthesis of boron phosphide

A new method of producing boron phosphide (BP) submicron powders by self-propagating high-temperature reaction between boron phosphate and magnesium in the presence of an inert diluent (sodium chloride) has been proposed. Bulk polycrystalline BP with microhardness of HV = 28(2) GPa has been prepared by sintering the above powders at 7.7 GPa and 2600 K.

preprint2014arXiv

Self-propagating high-temperature synthesis of boron subphosphide, B12P2

Two new methods to produce nanopowders of B12P2 boron subphosphide by self-propagating high-temperature synthesis have been proposed. Bulk polycrystalline B12P2 with microhardness of HV = 35(3) GPa and stability in air up to 1300 K has been prepared by sintering these powders at 5.2 GPa and 2500 K.

preprint2013arXiv

Comment on "Thermodynamic properties of rock-salt ZnO" by Leitner et al. [Thermochimica Acta 572 (2013) 1-5]

Very recently Leitner et al. [Thermochimica Acta 572 (2013) 1-5] have tried to extract the thermodynamic data of rock-salt ZnO from ab initio and experimental data available in the literature. In this Comment we show that neglecting (i) the strongly pronounced kinetic features of the pressure-induced phase transition in ZnO at room temperature and (ii) results of calorimetric measurements available in the literature [Russ. Chem. Bull. 59 (2010) 325-328] makes the proposed set of thermodynamic functions completely incorrect.

preprint2013arXiv

Low-temperature thermal expansion of rock-salt ZnO

Lattice parameter of metastable high-pressure phase of zinc oxide, rock-salt ZnO was measured in the 10-300 K temperature range using synchrotron X-ray powder diffraction. No phase transition was observed down to 10 K. The lattice parameter of rock-salt ZnO was found to increase from 4.266 Å in the 10-80 K range up to 4.2752(3) Å at 298 K, while the volume thermal expansion coefficient increases from slight negative values below 40 K up to 4.77\times10^-5 K^-1 at 298 K.

preprint2012arXiv

On melting of B4C boron carbide under pressure

The pressure dependence of melting temperatures for boron carbide and B4C-carbon eutectic has been studied up to 8 GPa, and it was found that in both cases the melting curves exhibit negative slope (-13\pm6 K/GPa), that is indicative of higher density of the melt as compared to the solid phase.