Magneto-transport and magnetic susceptibility of SmFeAsO1-xFx (x = 0.0 and 0.20)
Bulk polycrystalline samples, SmFeAsO and the iso-structural superconducting SmFeAsO0.80F0.20 are explored through resistivity with temperature under magnetic field ρ(T, H), AC and DC magnetization (M-T), and Specific heat (Cp) measurements. The Resistivity measurement shows superconductivity for x = 0.20 sample with Tc(onset) ~ 51.7K. The upper critical field, [Hc2(0)] is estimated ~3770kOe by Ginzburg-Landau (GL) theory. Broadening of superconducting transition in magneto transport is studied through thermally activated flux flow in applied field up to 130 kOe. The flux flow activation energy (U/kB) is estimated ~1215K for 1kOe field. Magnetic measurements exhibited bulk superconductivity with lower critical field (Hc1) of ~1.2kOe at 2K. In normal state, the paramagnetic nature of compound confirms no trace of magnetic impurity which orders ferromagnetically. AC susceptibility measurements have been carried out for SmFeAsO0.80F0.20 sample at various amplitude and frequencies of applied AC drive field. The inter-granular critical current density (Jc) is estimated. Specific heat [Cp(T)] measurement showed an anomaly at around 140K due to the SDW ordering of Fe, followed by another peak at 5K corresponding to the antiferromagnetic (AFM) ordering of Sm+3 ions in SmFeAsO compound. Interestingly the change in entropy (marked by the Cp transition height) at 5K for Sm+3 AFM ordering is heavily reduced in case of superconducting SmFeAsO0.80F0.20 sample.