Researcher profile

Yuji Tsuchiya

Yuji Tsuchiya contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

Trust snapshot

Quick read

Trust 21 - Emerging
17works
0followers
3topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

17 published item(s)

preprint2024arXiv

Single Crystal Growth and Transport Properties of van der Waals Materials $AB$Te$_\mathbf{4}$ ($A/B$ = Ti, Zr, Hf)

Monolayers of $AB$Te$_4$ ($A$/$B$ = Ti, Zr, Hf) were theoretically predicted to be two-dimensional topological insulators, but little has been known about the physical properties of these compounds. Here, we report on the single crystal growth, bulk transport properties, and band structure calculations of these compounds. The magnetotransport properties indicate that all three compounds are multi-carrier systems. The experimental results of ZrTiTe$_4$ and HfTiTe$_4$ can be well fitted by the multi-carrier formula assuming two types of carriers, while three carrier components were necessary for HfZrTe$_4$. Interestingly, one of the carrier mobilities of HfZrTe$_4$ exceeded 1000 cm$^2$V$^{-1}$s$^{-1}$, which was nearly one order in magnitude larger than the carrier mobilities of ZrTiTe$_4$ and HfTiTe$_4$. Our band structure calculations showed that all three compounds are semimetals consistent with the magnetotransport properties. The band structure around the $Γ$-point of HfZrTe$_4$ exhibits features that are distinct from the other two compounds, which is likely the reason of the different carrier properties.

preprint2016arXiv

Enhancement of critical current densities in (Ba,K)Fe2As2 wires and tapes using HIP technique

(Ba,K)Fe2As2 superconducting wires and tapes are fabricated by using hot isostatic pressing (HIP) technique, and their superconducting properties are studied. In the HIP round wire, transport critical current density (Jc) at 4.2 K has achieved record-high value of 175 kA/cm2 at zero field, and exceeds 20 kA/cm2 even at 100 kOe. Improvement of polycrystalline powder synthesis may play a key role for the enhancement of Jc. In the HIP tape, even larger transport Jc of 380 kA/cm2 is realized at zero field. Based on magnetization and magneto-optical measurements, possible further enhancement of Jc is discussed.

preprint2015arXiv

Evolution of superconducting and transport properties in annealed FeTe$_{1-x}$Se$_x$ (0.1 $\leq$ $x$ $\leq$ 0.4) multiband superconductors

We investigated the superconducting and transport properties in FeTe$_{1-x}$Se$_{x}$ (0.1 $\leq$ $x$ $\leq$ 0.4) single crystals prepared by O$_2$-annealing. Sharp superconducting transition width observed in magnetization measurement and the small residual resistivity prove the high quality of the crystals. All the crystals manifest large, homogeneous, and isotropic critical current density \emph{J}$_c$ with self-field value over 10$^5$ A/cm$^2$ at 2 K. The large and field-robust critical current densities prove that the superconductivity in FeTe$_{1-x}$Se$_{x}$ (0.1 $\leq$ $x$ $\leq$ 0.4) is in bulk nature. The values of anisotropy parameter close to $T_c$ for crystals with different Se doping levels all reside in the range of 2 - 3. Hall coefficients $R_H$ keeps positive and almost constant value at high temperatures, followed by a sudden decreases before reaching $T$$_c$, which indicates that the electron-type charge carriers become dominant at low temperatures. Furthermore, the characteristic temperature for the sudden decrease in $R_H$ gradually increases with Se doping.

preprint2014arXiv

Bulk Superconductivity in Fe1+yTe0.6Se0.4 Induced by Removal of Excess Fe

Experimental evidences from transport, magnetic, and magneto-optical (MO) image measurements confirmed that arsenic (As) vapor annealing was another effective way to induce bulk superconductivity with isotropic, large, and homogenous superconducting critical current density (Jc) in Fe1+yTe0.6Se0.4 single crystal. Since As is an exotic and easily detectable heavy element to Fe1+yTe0.6Se0.4 single crystal, As vapor annealing is very advantageous for the study of annealing mechanism. Detailed micro-structural and elemental analyses exclude the possibility that intercalating or doping effect may happen in the other post-annealing methods, proving that Fe reacts with As on the surface of the crystal and the reaction itself acts as a driving force to drag excess Fe out. The removal of excess Fe results in the good superconductivity performance.

preprint2014arXiv

Dynamics and mechanism of oxygen annealing in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystal

Iron chalcogenide Fe(Te,Se) attracted much attention due to its simple structure, which is favorable for probing the superconducting mechanism. Its less toxic nature compared with iron arsenides is also advantageous for applications of iron-based superconductors. By intercalating spacer layers, superconducting transition temperature has been raised over 40 K. On the other hand, the presence of excess Fe is almost unavoidable in Fe(Te,Se) single crystals, which hinders the appearance of bulk superconductivity and causes strong controversies over its fundamental properties. Here we report a systematical study of O$_2$-annealing dynamics in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ by controlling the amount of O$_2$, annealing temperature, and time. Bulk superconductivity can be gradually induced by increasing the amount of O$_2$ and annealing time at suitable temperatures. The optimally annealed crystals can be easily obtained by annealing with ~ 1.5% molar ratio of oxygen at 400 $^{\circ}$C for more than 1 hour. Superconductivity was witnessed to evolve mainly from the edge of the crystal to the central part. After the optimal annealing, the complete removal of excess Fe was demonstrated via STM measurements. Some fundamental properties were recharacterized and compared with those of as-grown crystals to discuss the influence of excess Fe.

preprint2014arXiv

Enhancement of transport critical current density of SmFeAsO1-xFx tapes fabricated by an ex-situ powder-in-tube method with a Sn-presintering process

SmFeAsO1-xFx (Sm1111) tapes were prepared by an ex-situ powder-in-tube method with a Sn-presintering process. Scanning electron microscopy revealed apparent difference in microstructure between Sn-presintered tapes and the previously reported polycrystalline Sm1111 bulk, since Sn has reduced FeAs wetting phase and filled the voids between Sm1111 grains. The Sn-presintered tapes showed significant enhanced field dependences of transport Jc compared with Sn-added tapes. A highest transport critical current density (Jc) of 3.45x10^4 A cm-2 at 4.2 K and self-field is achieved. Magneto-optical (MO) imaging further confirmed large and well-distributed global and intergranular Jc in Sn-presintered Sm1111 tapes.

preprint2014arXiv

Magneto-optical characterizations of FeTe$_{0.5}$Se$_{0.5}$ thin films with critical current density over 1 MA/cm$^2$

We performed magneto-optical (MO) measurements on FeTe$_{0.5}$Se$_{0.5}$ thin films grown on LaAlO$_3$ (LAO) and Yttria-stabilized zirconia (YSZ) single-crystalline substrates. These thin films show superconducting transition temperature, ${T_c}$ $\sim$ 19 K, 4 K higher than the bulk sample. Typical roof-top patterns can be observed in the MO images of thin films grown on LAO and YSZ, from which a large and homogeneous critical current density, ${J_c}$, over 1 $\times$ 10$^6$ A/cm$^2$ at 5 K was obtained. Magnetic flux penetration measurement reveals that the current is almost isotropically distributed in the two thin films. Compared with bulk crystals, FeTe$_{0.5}$Se$_{0.5}$ thin film demonstrates not only higher ${T_c}$, but also much larger ${J_c}$, which is attractive for applications.

preprint2013arXiv

Bulk Superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ Induced by Annealing in Se and S Vapor

We reported that bulk superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ can be induced by annealing in Se and S vapor. The well-annealed samples show a large critical current density, emph{J}$_c$ $\sim$ 2 - 4 $\times$ 10$^5$ A/cm$^2$. Combined with our previous reports about O$_2$ and Te annealing effects, we proved that bulk superconductivity can be successfully induced in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ by annealing in atmosphere of all chalcogens, such as O, S, Se and Te.

preprint2013arXiv

Enhancement of Critical Current Densities in (Ba,K)Fe2As2 by 320 MeV Au Irradiation in Single Crystals and by High-Pressure Sintering in PIT Wires

We demonstrate a large enhancement of critical current density (Jc) up to 1.0x10^7 A/cm2 at 5 K under self-field in (Ba,K)Fe2As2 single crystals by irradiating 320 MeV Au ions. With the very promising potential of this material in mind, we have fabricated a (Ba,K)Fe2As2 superconducting wire through a powder-in-tube method combined with the hot isostatic pressing technique, whose effectiveness has been proven in industrial Bi2223 tapes. The Jc in the wire at 4.2 K has reached 37 kA/cm2 under self-field and 3.0 kA/cm2 at 90 kOe. Magneto-optical imaging of the wire confirmed the large intergranular Jc in the wire core.

preprint2013arXiv

Evolution of Superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ Annealed in Te Vapor

We report a detailed study of the Te vapor annealing effect in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystals. Bulk superconductivity can be gradually induced by annealing with increasing amount of Te, until the molar ratio of Te to the sample reaches 1 : 10. By further increasing Te molar ratio, superconducting volume is gradually reduced. Resistivity and Hall effect measurements manifest that annealing in Te vapor delocalizes the charge carriers by removing excess Fe. The optimally Te annealed crystal shows homogeneous critical current densities with a large value of $\sim$ 4.3 $\times$ 10$^5$ A/cm$^2$, which proves that the Te annealing is effective to induce bulk superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$.

preprint2013arXiv

Large, Homogeneous, and Isotropic Critical Current Density in Oxygen-Annealed Fe1+yTe0.6Se0.4 Single Crystal

We reported a controllable way of removing excess Fe in Fe1+yTe0.6Se0.4 by annealing in a fixed amount of O2. Compared with the weak superconductivity induced by dilute acids, O2 annealing can successfully induce bulk superconductivity. Proper O2 annealing changes the temperature dependence of resistivity at low temperatures from semiconducting to metallic, which comes from the deintercalation of excess Fe. Critical current densities with field along the c-axis and ab-plane are found almost isotropic with large values of 3*10^5 A/cm2 and 2.5*10^5 A/cm2 at 2 K. Furthermore, magneto-optical images reveal isotropic current flow within the ab-plane.

preprint2013arXiv

Magnetic relaxation and collective vortex creep in FeTe$_{0.6}$Se$_{0.4}$ single crystal

We study the vortex dynamics in high-quality FeTe$_{0.6}$Se$_{0.4}$ single crystal by performing magnetization measurements of the screening current density \emph{J}$_s$ and flux creep rate \emph{S}. Temperature dependence of \emph{S} shows a plateau in the intermediate temperature region with a high creep rate $\sim$ 0.03, which is interpreted in the framework of the collective creep theory. A crossover from elastic to plastic creep is observed. The glassy exponent and barrier height for flux creep are directly determined by extended Maley's method. \emph{J}$_s$ with flux creep, obtained from magnetic hysteresis loops, is successfully reproduced based on the collective creep analysis. We also approach critical current density without flux creep by means of the generalized inversion scheme, which proves that the $δ$\emph{l} and $δ$\emph{T}$_c$ pinning coexist in FeTe$_{0.6}$Se$_{0.4}$ single crystal.

preprint2012arXiv

Anisotropies and Homogeneities of Superconducting Properties in Iron-Platinum-Arsenide Ca10(Pt3As8)(Fe1.79Pt0.21As2)5

We report a study on the anisotropy of superconducting properties in single crystalline Ca10(Pt4-δAs8)(Fe1.79Pt0.21As2)5 with Tc ~13.6 K. Under a field of 5 Oe, the sample reaches fully-diamagnetic state at ~10 K for H//c, and ~8 K for H//ab, indicating the presence of slight inhomogeneities. The magnetization measurements reveal fish-tail effect in the hysteresis loop for both H//c and H//ab. Averaged critical current densities at low magnetic fields along the c-axis and ab-plane Jc(H//c) and Jc(H//ab) at 5 K are estimated to be 0.9*10^5 and 0.7*10^5 A/cm2, respectively. Resistive transitions under magnetic field show broadening, which is consistent with a relatively large anisotropy of upper critical field. Magneto-optical images reveal homogenous current flow within the ab-plane.

preprint2012arXiv

Magnetic and transport properties of iron-platinum arsenide Ca10(Pt4-δAs8)(Fe2-xPtxAs2)5 single crystal

We report superconducting properties of single crystalline Ca10(Pt4-δAs8)(Fe2-xPtxAs2)5 by X-ray diffraction, magnetization, resistivity, and magneto-optical imaging measurements. The magnetization measurements reveal fish-tail hysteresis loop and relatively high critical current density Jc ~ 0.8\times105 A/cm2 at low temperatures. The exponential temperature dependence of Jc, which arises from nonlinear effective flux-creep activation energy, has been observed. Upper critical field determined by resistive transition shows a relatively large anisotropy. The magneto-optical images reveal homogenous current flow within the crystal.

preprint2012arXiv

Superconducting properties and magneto-optical imaging of Ba0.6K0.4Fe2As2 PIT wires with Ag addition

We have fabricated (Ba,K)Fe2As2 superconducting wires through ex-situ powder-in-tube method. Silver was used as a chemical addition to improve the performance of these superconducting wires. The transport critical current densities (Jc) have reached 1.3\times104 A/cm and 1.0\times104 A/cm2 at 4.2 K under self field in the wires with and without Ag addition. We used magneto-optical (MO) imaging technique to investigate the properties of grain boundaries in the (Ba,K)Fe2As2 superconducting wire with Ag addition. MO images show the weak links in the Fe-based superconducting wires for the first time. An intragranular Jc of 6.0\times104 A/cm2 at 20 K is obtained from MO image, which is consistent with the estimation from M-H measurement.

preprint2011arXiv

Instability of vortex-antivortex interface in optimally-doped Ba(Fe_{1-x}Co_{x})_{2}As_{2}

We explore the flux front patterns during virgin penetration and after remagnetization in the iron-based superconductor Ba(Fe_{1-x}Co_{x})_{2}As_{2}. After remagnetization we observe an instability characterized by turbulent dynamics at the vortex-antivortex boundary. Associated with the turbulent flux boundary a band of excess current density is observed. The turbulence is contrasted with the instability observed in the cuprate superconductors. Our results suggest turbulent instability at the vortex-antivortex interface may be a common feature in all remagnetized type-II superconductors.

preprint2011arXiv

Low-temperature Synthesis of FeTe0.5Se0.5 Polycrystals with a High Transport Critical Current Density

We have prepared high-quality polycrystalline FeTe0.5Se0.5 at temperature as low as 550°C. The transport critical current density evaluated by the current-voltage characteristics is over 700 A/cm2 at 4.2 K under zero field, which is several times larger than FeTe0.5Se0.5 superconducting wires. The critical current density estimated from magneto-optical images of flux penetration is also similar to this value. The upper critical field of the polycrystalline FeTe0.5Se0.5 at T = 0 K estimated by Werthamer-Helfand-Hohenberg theory is 585 kOe, which is comparable to that of single crystals. This study gives some insight into how to improve the performance of FeTe0.5Se0.5 superconducting wires.