Researcher profile

T. Petrisor Jr

T. Petrisor Jr contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

Trust snapshot

Quick read

Trust 17 - UnverifiedVerification L1Unclaimed author
4works
0followers
1topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Identity and collaboration

How to connect with this researcher

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Log in to claim

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

4 published item(s)

preprint2014arXiv

Co2FeAl Heusler thin films grown on Si and MgO substrates: annealing temperature effect

10 nm and 50 nm Co$_{2}$FeAl (CFA) thin films have been deposited on MgO(001) and Si(001) substrates by magnetron sputtering and annealed at different temperatures. X-rays diffraction revealed polycrystalline or epitaxial growth (according to the relation CFA(001)[110]//MgO(001)[100] epitaxial relation), respectively for CFA films grown on a Si and on a MgO substrate. For these later, the chemical order varies from the A2 phase to the B2 phase when increasing the annealing temperature (Ta) while only the A2 disorder type has been observed for CFA grown on Si. Microstrip ferromagnetic resonance (MS-FMR) measurements revealed that the in-plane anisotropy results from the superposition of a uniaxial and of a fourfold symmetry term for CFA grown on MgO substrates. This fourfold anisotropy, which disappears completely for samples grown on Si, is in accord with the crystal structure of the samples. The fourfold anisotropy field decreases when increasing Ta while the uniaxial anisotropy field is nearly unaffected by Ta within the investigated range. The MS-FMR data also allow for concluding that the gyromagnetic factor remains constant and that the exchange stiffness constant increases with $T_{a}$. Finally, the FMR linewidth decreases when increasing Ta, due to the enhancement of the chemical order. We derive a very low intrinsic damping parameter (1.3*10^-3 and 1.1*10^-3 for films of 50 nm thickness annealed at 615 °C grown on MgO and on Si, respectively).

preprint2014arXiv

Magnetic and structural properties of Co2FeAl thin films grown on Si substrate

The correlation between magnetic and structural properties of Co_{2} FeAl (CFA) thin films of different thickness (10 nm<d< 100 nm) grown at room temperature on MgO-buffered Si/SiO2 substrates and annealed at 600\lyxmathsym{\textdegree}C has been studied. XRD measurements revealed an (011) out-of-plane texture growth of the films. The deduced lattice parameter increases with the film thickness. Moreover, pole figures showed no in-plane preferential growth orientation. The magneto-optical Kerr effect hysteresis loops showed the presence of a weak in-plane uniaxial anisotropy with a random easy axis direction. The coercive field measured with an applied field along the easy axis direction and the uniaxial anisotropy field increase linearly with the inverse of the CFA thickness. The microstrip line ferromagnetic resonance measurements for in-plane and perpendicular applied magnetic fields revealed that the effective magnetization and the uniaxial in-palne anisotropy field follow a linear variation versus the inverse CFA thickness. This allows deriving a perpendicular surface anisotropy coefficient of -1.86 erg/cm2

preprint2013arXiv

Co2 FeAl thin films grown on MgO substrates: Correlation between static, dynamic and structural properties

Co2FeAl (CFA) thin films with thickness varying from 10 nm to 115 nm have been deposited on MgO(001) substrates by magnetron sputtering and then capped by Ta or Cr layer. X-rays diffraction (XRD) revealed that the cubic $[001]$ CFA axis is normal to the substrate and that all the CFA films exhibit full epitaxial growth. The chemical order varies from the $B2$ phase to the $A2$ phase when decreasing the thickness. Magneto-optical Kerr effect (MOKE) and vibrating sample magnetometer measurements show that, depending on the field orientation, one or two-step switchings occur. Moreover, the films present a quadratic MOKE signal increasing with the CFA thickness, due to the increasing chemical order. Ferromagnetic resonance, MOKE transverse bias initial inverse susceptibility and torque (TBIIST) measurements reveal that the in-plane anisotropy results from the superposition of a uniaxial and of a fourfold symmetry term. The fourfold anisotropy is in accord with the crystal structure of the samples and is correlated to the biaxial strain and to the chemical order present in the films. In addition, a large negative perpendicular uniaxial anisotropy is observed. Frequency and angular dependences of the FMR linewidth show two magnon scattering and mosaicity contributions, which depend on the CFA thickness. A Gilbert damping coefficient as low as 0.0011 is found.

preprint2012arXiv

Reduction of spin polarization by incoherent tunneling in Co2FeAl/MgO/CoFe magnetic tunnel junctions with thick MgO barriers

We report on spin polarization reduction by incoherent tunneling in realistic single crystal Co2FeAl/MgO/Co50Fe50 magnetic tunnel junctions (MTJ) compared to reference Fe/MgO/Fe. A large density of misfit dislocations in the Heusler based MTJs has been insured by a thick MgO barrier and its 3.8% lattice mismatch with the Co2FeAl electrode. Our analysis implicates a correlated structural-transport approach. The crystallographic coherence, in the real space, is investigated using High Resolution Transmission Electron Microscopy phase analysis. The electronic transport experiments in variable temperature, fitted with a theoretical extended-Glazman-Matveev model, address different levels of the tunneling mechanisms from direct to multi-center hopping. We demonstrate a double negative impact of dislocations, as extended defects, on the tunneling polarization. Firstly, the breaking of the crystal symmetry destroys the longitudinal and lateral coherence of the propagating Bloch functions. This affects the symmetry filtering efficiency of the Delta_1 states across the (100) MgO barriers and reduces the associated effective tunneling polarization. Secondly, dislocations provide localized states within the MgO gap. This determines temperature activated spin-conserving inelastic tunneling through chains of defects which are responsible for the one order of magnitude drop of the tunnel magnetoresistance from low to room temperature.