Source author record

S. K. Agarwal

S. K. Agarwal appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci cond-mat.str-el

Catalog footprint

What is connected

3works

2topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2015arXiv

Structural, Magnetic and Magneto-caloric studies of Ni50Mn30Sn20Shape Memory Alloy

We have synthesized a nominal composition of Ni50Mn30Sn20 alloy using arc melting technique. Rietveld refinement confirms the austenite L21 structure in Fm-3m space group. Electrical resistivity has been found to clearly exhibiting two different phenomena viz. a magnetic transition from paramagnetic to ferromagnetic and a structural transition from austenite to martensitic phase. Thermo-magnetization measurements M(T) confirms ferromagnetic transition temperature TC at 222 K and martensitic transition starting at 127 K(MS). Magnetization measurement M(H) at 10 K confirms the ferromagnetic state. Frequency dependence of ac susceptibility \c{hi}' at low temperature suggests spin glass behavior in the system. The isothermal magnetic entropy change values have been found to be 1.14 J/Kg.K, 2.69 J/Kg.K and 3.9 J/Kg.K, with refrigeration capacities of 19.6 J/kg, 37.8 J/kg and 54.6 J/kg for the field change of 1, 2 and 3 Tesla respectively at 227 K.

preprint2013arXiv

Impact of sintering temperature on room temperature magneto-resistive and magneto-caloric properties of Pr2/3Sr1/3MnO3

Magneto-resistive and magneto-caloric properties of polycrystalline Pr2/3Sr1/3MnO3 have been studied as a function of sintering temperature (Ts) between 1260-1450°C. Reitveld refinement of their X-ray diffraction (XRD) patterns confirms their single phase crystalline structure with orthorhombic Pbnm space group. The point of maximum value of temperature coefficient of resistance (TCRmax) and Curie temperature (Tc) decreased slightly with Ts. Magneto-resistance (MR) and magnetic entropy (ΔSM) increased markedly with sintering temperature. This could be attributed to the observed sharpness of both the magnetic and resistive transitions due to better grain connectivity. Optimum results are obtained for the sample with Ts = 1400°C. MR at Tc of the same is found to be as large as 32% at 1T and 58% at 5T magnetic fields. The maximum entropy change (ΔSMmax) near its Tc is 2.3Jkg-1K-1 and 7.8 Jkg-1K-1 upon 1T and 5T fields change respectively. These characteristics [MR (32% 1T, 58% 5T) and reasonable change in magnetic entropy (7.8Jkg-1K-1, 5T)] generate possibility that the optimized compound can be used as a potential magnetic refrigerant close to room temperature.

preprint2012arXiv

Enhanced Room Temperature Coefficient of Resistance and Magneto-resistance of Ag-added La0.7Ca0.3-xBaxMnO3 Composites

In this paper we report an enhanced temperature coefficient of resistance (TCR) close to room temperature in La0.7Ca0.3-xBaxMnO3 + Agy (x = 0.10, 0.15 and y = 0.0 to 0.40) (LCBMO+Ag) composite manganites. The observed enhancement of TCR is attributed to the grain growth and opening of new conducting channels in the composites. Ag addition has also been found to enhance intra-granular magneto-resistance. Inter-granular MR, however, is seen to decrease with Ag addition. The enhanced TCR and MR at / near room temperature open up the possibility of the use of such materials as infrared bolometric and magnetic field sensors respectively.