Infrared absorption study has been carried out on a series of half doped manganites, La0.5Ca0.5−xSrxMnO3 (0.1≤x≤0.5), with varying magnetic ground state. The charge ordering transition observed in samples with {\normalsize x≤0.3 is accompanied by a mode at ∼525cm−1 in addition to the stretching mode at 615cm−1 and bending mode at 400cm−1. Phonon hardening is found to occur below the CE - type antiferromagnetic ordering temperature. The value of the insulating gap decreases on doping with Sr from 727cm−1 to 615cm−1.}
This paper reports effect of thermally induced disorder on the magnetic properties of LaSrCoRuO6 double perovskite. While the ordered sample is antiferromagnetic, the disordered sample exhibits negative values of magnetization measured in low applied fields. Isothermal magnetization on this sample shows hysteresis due to presence of ferromagnetic interactions. Based on neutron diffraction and X-ray Absorption Fine Structure (XAFS) studies, these results have been interpreted to be due disorder in site occupancy of Co and Ru leading to octahedral distortions and formation of Ru-O-Ru ferromagnetic linkages. Below 150K these ferromagnetic Ru spins polarize the Co spins in a direction opposite to that of the applied field resulting in observed negative magnetization.
The perovskite solid solutions of the type La2xSr2−2xCo2xRu2−2xO6 with 0.25 ≤ x ≤ 0.75 have been investigated for their structural, magnetic and transport properties. All the compounds crystallize in double perovskite structure. The magnetization measurements indicate a complex magnetic ground state with strong competition between ferromagnetic and antiferromagnetic interactions. Resistivity of the compounds is in confirmation with hopping conduction behaviour though differences are noted especially for x = 0.4 and 0.6. Most importantly, low field (50Oe) magnetization measurements display negative magnetization during the zero field cooled cycle. X-ray photoelectron spectroscopy measurements indicate presence of Co2+/Co3+ and Ru4+/Ru5+ redox couples in all compositions except x = 0.5. Presence of magnetic ions like Ru4+ and Co3+ gives rise to additional ferromagnetic (Ru-rich) and antiferromagnetic sublattices and also explains the observed negative magnetization.
Research graph
Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.
BZPEER is loading the nearby papers, people, topics and institutions for this page.