Anisotropic $H_{c2}$ determined up to 92 T and the signature of multi-band superconductivity in Ca$_{10}$(Pt$_{4}$As$_{8}$)((Fe$_{1-x}$Pt$_{x}$)$_{2}$As$_{2}$)$_{5}$ superconductor
The upper critical fields, $H_{c2}$($T$), of single crystals of the superconductor Ca$_{10}$(Pt$_{4-δ}$As$_{8}$)((Fe$_{0.97}$Pt$_{0.03}$)$_{2}$As$_{2}$)$_{5}$ ($δ$ $\approx$ 0.246) are determined over a wide range of temperatures down to $T$ = 1.42 K and magnetic fields of up to $μ_{0}H$ $\simeq$ 92 T. The measurements of anisotropic $H_{c2}$($T$) curves are performed in pulsed magnetic fields using radio-frequency contactless penetration depth measurements for magnetic field applied both parallel and perpendicular to the \textbf{ab}-plane. Whereas a clear upward curvature in $H_{c2}^{\parallel\textbf{c}}$($T$) along \textbf{H}$\parallel$\textbf{c} is observed with decreasing temperature, the $H_{c2}^{\parallel\textbf{ab}}$($T$) along \textbf{H}$\parallel$\textbf{ab} shows a flattening at low temperatures. The rapid increase of the $H_{c2}^{\parallel\textbf{c}}$($T$) at low temperatures suggests that the superconductivity can be described by two dominating bands. The anisotropy parameter, $γ_{H}$ $\equiv$ $H_{c2}^{\parallel\textbf{ab}}/H_{c2}^{\parallel\textbf{c}}$, is $\sim$7 close to $T_{c}$ and decreases considerably to $\sim$1 with decreasing temperature, showing rather weak anisotropy at low temperatures.