M. Fujioka

Explore this author’s publications, collaborators and research topics. This catalog record has not been claimed by its author.

ResearcherUnclaimed source record

cond-mat.supr-con cond-mat.str-el

Catalog footprint

Research overview

4works

2topics

4close collaborators

Actions

Is this your work?

Open graph Browse papers

preprint2014arXiv

Pressure-dependent magnetization and magnetoresistivity studies on the tetragonal FeS (mackinawite): revealing its intrinsic metallic character

The transport and magnetic properties of the tetragonal Fe $_{1+δ}$ S were investigated using magnetoresistivity and magnetization within 2 $\leq T\leq$ 300 K, $H\leq$ 70 kOe and $P\leq$ 3.0 GPa. In addition, room-temperature X-ray diffraction and photoelectron spectroscopy were also applied. In contrast to previously reported nonmetallic character, Fe $_{1+δ}$ S is intrinsically metallic but due to a presence of a weak localization such metallic character is not exhibited below room temperature. An applied pressure reduces strongly this additional resistive contribution and as such enhances the temperature range of the metallic character which, for $\sim$ 3 GPa, is evident down to 75 K. The absence of superconductivity as well as the mechanism behind the weak localization will be discussed.

preprint2013arXiv

Sulfur annealing effect for superconductivity in iron chalcogenide compounds

We discovered a novel annealing method for Fe-chalcogenide superconductors. It was found that sulfur annealing deintercalated excess Fe via formation of FeS2. Due to its specifics, sulfur annealing is applicable when preparing Fe-chalcogenide-based wires or cables.

preprint2012arXiv

Evolution of superconductivity in LaO1-xFxBiS2 prepared by high pressure technique

Novel BiS2-based superconductors LaO1-xFxBiS2 prepared by the high pressure synthesis technique were systematically studied. It was found that the high pressure annealing strongly the lattice as compared to the LaO1-xFxBiS2 samples prepared by conventional solid state reaction at ambient pressure. Bulk superconductivity was observed within a wide F-concentration range of x = 0.2 ~ 0.7. On the basis of those results, we have established a phase diagram of LaO1-xFxBiS2.

preprint2012arXiv

Superconductivity in Fe1+dTe0.9Se0.1 induced by deintercalation of excess Fe using alcoholic beverage treatment

Superconductivity in polycrystalline Fe1+dTe0.9Se0.1 was enhanced by heating in alcoholic beverages. We found that part of the excess Fe was deintercalated from the interlayer sites by the treatment and the shielding volume fractions were increased with the reduction of excess Fe content in sample. This behavior is similar to the case of Fe1+dTe1-xSx. Thus the technique of alcoholic beverage treatment can be applied generally to the Fe-chalcogenide superconductors.