BZPEERReading, trust and collaboration for researchDiscover
Workspaces
Network
Opportunities
Account
Researcher profile
H. Okazaki contributes to research discovery and scholarly infrastructure.
Trust snapshot
Actions
Identity and collaboration
Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.
Log in to claimDirect collaboration
Claim this author entity first to unlock direct invitations.
Research graph
Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.
BZPEER is loading the nearby papers, people, topics and institutions for this page.
Published work
We discovered a novel annealing method for Fe-chalcogenide superconductors. It was found that sulfur annealing deintercalated excess Fe via formation of FeS2. Due to its specifics, sulfur annealing is applicable when preparing Fe-chalcogenide-based wires or cables.
To elucidate the mechanism as to why alcoholic beverages can induce superconductivity in Fe_{1+d}Te_{1-x}S_x samples, we performed component analysis and found that weak acid such as organic acid has the ability to induce superconductivity. Inductively-coupled plasma spectroscopy was performed on weak acid solutions post annealing. We found that the mechanism of inducement of superconductivity in Fe_{1+d}Te_{1-x}S_x is the deintercalation of excess Fe from the interlayer sites.
Novel BiS2-based superconductors LaO1-xFxBiS2 prepared by the high pressure synthesis technique were systematically studied. It was found that the high pressure annealing strongly the lattice as compared to the LaO1-xFxBiS2 samples prepared by conventional solid state reaction at ambient pressure. Bulk superconductivity was observed within a wide F-concentration range of x = 0.2 ~ 0.7. On the basis of those results, we have established a phase diagram of LaO1-xFxBiS2.
Phase diagrams of as-grown and O2-annealed FeTe1-xSex determined from magnetic susceptibility measurement were obtained. For as-grown samples, the antiferromagnetic order was fully suppressed in the range region x \geq 0.15, and weak superconductivity appeared when x \geq 0.1. Beginning at x = 0.5, weak superconductivity was found to evolve into bulk superconductivity. Interestingly, for O2-annealed samples, complete suppression of magnetic order and the occurrence of bulk superconductivity were observed when x \geq 0.1. We found that O2-annealing induces bulk superconductivity for FeTe1-xSex. Oxygen probably plays a key role in the suppression of the magnetic order and the appearance of bulk superconductivity.
Superconductivity in polycrystalline Fe1+dTe0.9Se0.1 was enhanced by heating in alcoholic beverages. We found that part of the excess Fe was deintercalated from the interlayer sites by the treatment and the shielding volume fractions were increased with the reduction of excess Fe content in sample. This behavior is similar to the case of Fe1+dTe1-xSx. Thus the technique of alcoholic beverage treatment can be applied generally to the Fe-chalcogenide superconductors.
We use photoemission spectroscopy to study electronic structures of pristine and K-doped solid picene. The valence band spectrum of pristine picene consists of three main features with no state at the Fermi level (EF), while that of K-doped picene has three structures similar to those of pristine picene with new states near EF, consistent with the semiconductor-metal transition. The K-induced change cannot be explained with a simple rigid-band model of pristine picene, but can be interpreted by molecular orbital calculations considering electron-intramolecular-vibration interaction. Excellent agreement of the K-doped spectrum with the calculations points to importance of electron-intramolecular-vibration interaction in K-doped picene.