Source author record

M. D. Mukadam

M. D. Mukadam appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci cond-mat.str-el

Catalog footprint

What is connected

3works

2topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2016arXiv

Revealing the nature of magnetic phases in the semi-Heusler alloy Cu0.85Ni0.15MnSb

We report the magnetic, magnetocaloric, and magnetotransport properties of the semi-Heusler alloy Cu0.85Ni0.15MnSb, which exhibits coexistence of antiferromagnetic (AFM) and ferromagnetic (FM) phases. A broad magnetic phase transition is evident from the temperature variations of magnetization, heat capacity, and isothermal magnetic entropy change. This is due to the presence of both AFM and FM phases at low temperatures. The variation of electrical resistivity with temperature shows three distinct regions of magnetic phases. The magnetoresistance (MR) results also show the presence of AFM and FM phases at temperatures below 45 K, and a FM phase at temperature above 45K. Though there is no signature of a spin-glass state at low temperatures, various results point towards the presence of short-range magnetic correlations at low temperatures.

preprint2011arXiv

Magnetocaloric effect and critical behavior near the paramagnetic to ferrimagnetic phase transition temperature in TbCo2-xFex

Magnetocaloric effect (MCE) in TbCo2-xFex has been studied by dc magnetization measurements.On substituting Fe in TbCo2, not only the magnetic transition temperature is tuned to room temperature, but also the operating temperature range for MCE is increased from 50 K for TbCo2 to 95 K for TbCo1.9Fe0.1. The maximum magnetic entropy change (-ΔSM) for TbCo1.9Fe0.1 is found to be 3.7 J kg-1 K-1 for a 5 T field change, making it a promising candidate for magnetic refrigeration near room temperature. The temperature dependent neutron diffraction study shows a structural phase transition (from cubic to rhombohedral phase with lowering of temperature) which is associated with the magnetic phase transition and these transitions broaden on Fe substitution. To investigate the nature of the paramagnetic to ferrimagnetic phase transition, we performed a critical exponent study. From the derived values of critical exponents, we conclude that TbCo2 belongs to the 3D Heisenberg class with short-range interaction, while on Fe substitution it tends towards mean-field with long-range interaction. The derived values of critical exponents represent the phenomenological universal curve for the field dependence of ΔSM, indicating that TbCo2 and TbCo1.9Fe0.1 belong to two different universality classes.

preprint2010arXiv

Defects induced ferromagnetism in Mn doped ZnO

Single phase Mn doped (2 at %) ZnO samples have been synthesized by solid-state reaction technique. Before the final sintering at 500 C, the mixed powders have been milled for different milling periods (6, 24, 48 and 96 hours). The grain sizes of the samples are very close to each other (~ 32 \pm 4 nm). However, the defective state of the samples is different from each other as manifested from the variation of magnetic properties and electrical resistivity with milling time. All the samples have been found to be ferromagnetic with clear hysteresis loops at room temperature. The maximum value for saturation magnetization (0.11 μ_B / Mn atom) was achieved for 96 hours milled sample. Electrical resistivity has been found to increase with increasing milling time. The most resistive sample bears the largest saturation magnetization. Variation of average positron lifetime with milling time bears a close similarity with that of the saturation magnetization. This indicates the key role played by open volume vacancy defects, presumably zinc vacancies near grain surfaces, in inducing ferromagnetic order in Mn doped ZnO. To attain optimum defect configuration favorable for ferromagnetism in this kind of samples proper choice of milling period and annealing conditions is required.