Source author record

Ingrid Hallsteinsen

Ingrid Hallsteinsen appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

Catalog footprint

What is connected

3works
3topics
4close collaborators

Actions

Connect this record

Log in to claim

Research graph

See the researcher in context

Open full explorer

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

3 published item(s)

preprint2020arXiv

Effect of strain on magnetic and orbital ordering of LaSrCrO$_3$/LaSrMnO$_3$ heterostructures

We investigate the effect of strain and film thickness on the orbital and magnetic properties of LaSrCrO$_3$ (LSCO)/LaSrMnO$_3$ (LSMO) heterostructures using bulk magnetometry, soft X-ray magnetic spectroscopy, first-principles density functional theory, high-resolution electron microscopy and X-ray diffraction. We observe an anti-parallel ordering of the magnetic moments between the ferromagnetic LSMO layers and the LSCO spacers leading to a strain-independent ferromagnetic ground state of the LSCO/LSMO heterostructures for LSMO layers as thin as 2 unit cells. As the LSMO thickness is increased, a net ferromagnetic state is maintained, however, the average magnetic moment per Mn is found to be dependent on the magnitude of the substrate-induced strain. The differences in the magnetic responses are related to preferential occupation of the Mn $x^2-y^2$ (in-plane) d-orbitals for tensile strain and $3z^2-r^2$ (out-of-plane) orbitals under compressive strain leading to competing ferromagnetic and anti-ferromagnetic exchange interactions within the LSMO layers. These results underscore the relative contributions of orbital, structural and spin degree of freedom and their tunability in atomically-thin crystalline complex oxide layers.

preprint2016arXiv

Assessing electron beam sensitivity for SrTiO$_3$ and La$_{0.7}$Sr$_{0.3}$MnO$_3$ using electron energy loss spectroscopy

Thresholds for beam damage have been assessed for La$_{0.7}$Sr$_{0.3}$MnO$_3$ and SrTiO$_3$ as a function of electron probe current and exposure time at 80 and 200 kV acceleration voltage. The materials were exposed to an intense electron probe by aberration corrected scanning transmission electron microscopy (STEM) with simultaneous acquisition of electron energy loss spectroscopy (EELS) data. Electron beam damage was identified by changes of the core loss fine structure after quantification by a refined and improved model based approach. At 200 kV acceleration voltage, damage in SrTiO$_3$ was identified by changes both in the EEL fine structure and by contrast changes in the STEM images. However, the changes in the STEM image contrast as introduced by minor damage can be difficult to detect under several common experimental conditions. No damage was observed in SrTiO$_3$ at 80 kV acceleration voltage, independent of probe current and exposure time. In La$_{0.7}$Sr$_{0.3}$MnO$_3$, beam damage was observed at both 80 and 200 kV acceleration voltages. This damage was observed by large changes in the EEL fine structure, but not by any detectable changes in the STEM images. The typical method to validate if damage has been introduced during acquisitions is to compare STEM images prior to and after spectroscopy. Quantifications in this work show that this method possibly can result in misinterpretation of beam damage as changes of material properties.

preprint2016arXiv

Thickness and temperature dependence of the magnetodynamic damping of pulsed laser deposited $\text{La}_{0.7}\text{Sr}_{0.3}\text{MnO}_3$ on (111)-oriented SrTi$\text{O}_3$

We have investigated the magnetodynamic properties of $\text{La}_{0.7}\text{Sr}_{0.3}\text{MnO}_3$ (LSMO) films of thickness 10, 15 and 30 nm grown on (111)-oriented SrTi$\text{O}_3$ (STO) substrates by pulsed laser deposition. Ferromagnetic resonance (FMR) experiments were performed in the temperature range 100--300 K, and the magnetodynamic damping parameter $α$ was extracted as a function of both film thickness and temperature. We found that the damping is lowest for the intermediate film thickness of 15 nm with $α\approx 2 \cdot 10^{-3}$, where $α$ is relatively constant as a function of temperature well below the Curie temperature of the respective films.