Tin telluride: a weakly co-elastic metal

We report resonant ultrasound spectroscopy (RUS), dilatometry/magnetostriction, magnetotransport, magnetization, specific heat, and $^{119}$Sn Mössbauer spectroscopy measurements on SnTe and Sn$_{0.995}$Cr$_{0.005}$Te. Hall measurements at $T=77$ K indicate that our Bridgman-grown single crystals have a $p$-type carrier concentration of $3.4 \times 10^{19}$ cm$^{-3}$ and that our Cr-doped crystals have an $n$-type concentration of $5.8 \times 10^{22}$ cm$^{-3}$. Although our SnTe crystals are diamagnetic over the temperature range $2\, \text{K} \leq T \leq 1100\, \text{K}$, the Cr-doped crystals are room temperature ferromagnets with a Curie temperature of 294 K. For each sample type, three-terminal capacitive dilatometry measurements detect a subtle 0.5 micron distortion at $T_c \approx 85$ K. Whereas our RUS measurements on SnTe show elastic hardening near the structural transition, pointing to co-elastic behavior, similar measurements on Sn$_{0.995}$Cr$_{0.005}$Te show a pronounced softening, pointing to ferroelastic behavior. Effective Debye temperature, $θ_D$, values of SnTe obtained from $^{119}$Sn Mössbauer studies show a hardening of phonons in the range 60--115K ($θ_D$ = 162K) as compared with the 100--300K range ($θ_D$ = 150K). In addition, a precursor softening extending over approximately 100 K anticipates this collapse at the critical temperature, and quantitative analysis over three decades of its reduced modulus finds $ΔC_{44}/C_{44}=A|(T-T_0)/T_0|^{-κ}$ with $κ= 0.50 \pm 0.02$, a value indicating a three-dimensional softening of phonon branches at a temperature $T_0 \sim 75$ K, considerably below $T_c$. We suggest that the differences in these two types of elastic behaviors lie in the absence of elastic domain wall motion in the one case and their nucleation in the other.

No reviews yet.

No comments yet.