Abstract
The results of XPS core-level and valence band measurements, photoluminescence spectra of a-SiO2 implanted by Zn-ions (E=30 keV, D=1*1017 cm^-2) and Density Functional Theory calculations of electronic structure as well as formation energies of structural defects in silica glass induced by Zn-ion implantation are presented. Both theory and experiment show that it is energetically more favorable for implanted zinc ions to occupy the interstitial positions instead of cation substitution. As a result, the Zn-ions embedded to interstitials, form chemical bonds with the surrounding oxygen atoms, formation ZnO-like nanoparticles and oxygen-deficient SiOx matrix. The subsequent thermal annealing at 900 0C (1 hr) strongly reduces the amount of ZnO nanoparticles and induces the formation of α-Zn2SiO4 phase which markedly enhances the green emission.
Connections
Explore this paper’s authors, topics and related work.
Building this map preview
BZPEER is loading the nearby papers, people, topics and institutions for this page.
Reviews 0
Write a review
No reviews yet.
Discussion 0
Add a comment
No comments yet.