Source author record

Vinay Kumar Shukla

Vinay Kumar Shukla appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.str-el cond-mat.mtrl-sci

Catalog footprint

What is connected

3works

2topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2016arXiv

Anomalous ferroelectric switching dynamics in single crystalline SrTiO3

Pure SrTiO3 in bulk form is known to be an incipient ferroelectric where the quantum fluctuations of lattice positions prevent long range ferroelectric ordering at a finite temperature. We show evidence and identify the origin of ferroelectric relaxation up to nearly room temperature in single crystalline SrTiO3. Strikingly, the origin of the observed ferroelectric switching is intrinsic which is the coherent switching of surface nanopolar regions and not due to the nucleation and growth of domains, as described by the Kolmogorov-Avrami-Ishibashi Model.

preprint2016arXiv

Emergence of ferroelectric switching in self organized Pr0.67Ca0.33MnO3 nanocrystal array

We discuss the emergence of low dimensional ferroelectricity in self-organized Pr0.67Ca0.33MnO3 nanocrystalline arrays deposited on Si substrate. We observe sharp switching of electric polarization under external electric eld with nearly rectangular hysteresis loops which persist up to 150 K. We discuss the polarization switching kinetics within the framework of Kolmogorov-Avrami-Ishibashi Model which gives maximum domain wall speed of ~1 m/s. Polarized Raman spectroscopy shows evidence of isolated ferroelectric domains even at room temperature.

preprint2014arXiv

Direct experimental evidence of multiferroicity in a nanocrystalline Zener polaron ordered manganite

We discuss the particle size driven tunability of the coexistence of ferromagnetism and ferroelectricity in Pr0.67Ca0.33MnO3(PCMO) with the help of x ray diffraction, magnetization, impedance spectroscopy, and remanent polarization measurements. The remanent polarization measurements using the positive up negative down method clearly prove the existence of ferroelectricity in PCMO with phase separation between Zener polaron(ZP) ordered P21nm and disordered Pbnm structures. We also find that the ferroelectric response is enhanced in nanocrystalline samples so long as ZP ordering is not destroyed while the long-range antiferromagnetic ordering at low temperature in bulk system is replaced by ferromagnetic correlations in nanoparticles. The conclusion that by reducing the crystallite size it might be possible to make ferromagnetism and ferroelectricity coexist near room temperature should be generally applicable to all ZP ordered manganites.