Researcher profile

Thomas Ryll

Thomas Ryll contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

Trust snapshot

Quick read

Trust 19 - UnverifiedVerification L1Unclaimed author
5works
0followers
3topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Identity and collaboration

How to connect with this researcher

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Log in to claim

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

5 published item(s)

preprint2014arXiv

Pt-based nanowire networks with enhanced oxygen-reduction activity

Pt-Al and Pt-Y-Al thin film electrodes on yttria-stabilised zirconia electrolytes were prepared by dealloying of co-sputtered Pt-Al or Pt-Y-Al films. The selective dissolution of Al from the Pt-alloy compound causes the formation of a highly porous nanowire network with a mean branch thickness below 25 nm and a pore intercept length below 35 nm. The oxygen reduction capability of the resulting electrodes was analysed in a micro-solid oxide fuel cell setup at elevated temperatures (598-873 K). Here, we demonstrate that these nanoporous thin films excel "state-of-the-art" fuel cell electrodes in terms of catalytic activity and thermal stability. The nanoporous Pt electrodes exhibit exchange current densities that are up to 13 times higher than conventional Pt electrodes, measured at 648 K. It is shown that the enhanced catalytic activity of these Pt electrodes is achieved through the engineering of the materials d-bands due to the addition of yttrium as ternary constituent.

preprint2012arXiv

Temperature-dependent 2D-3D growth transition of ultra-thin Pt films deposited by PLD

During the growth of metal thin films on dielectric substrates at a given deposition temperature T, the film's morphology is conditioned by the magnitude and asymmetry of up- and downhill diffusion. Any severe change of this mechanism leads to a growth instability, which induces an alteration of the thin film morphology. In order to study this mechanism, ultra-thin Pt films were deposited via pulsed laser deposition (PLD) onto yttria-stabilized-zirconia single crystals at different deposition temperatures. The morphological evolution of Pt thin films has been investigated by means of scanning electron microscopy (SEM), atomic force microscopy (AFM) and standard image analysis techniques. The experimentally obtained morphologies are compared to simulated thin film structures resulting from a two-dimensional kinetic Monte Carlo (KMC) approach. Two main observations have been made: i) Thin Pt films deposited onto zirconia undergo a growth transition from two-dimensional to three-dimensional growth at T > 573 K. The growth transition and related morphological changes are a function of the deposition temperature. ii) A critical cluster size of i\ast = 4 in combination with an asymmetric Ehrlich-Schwoebel (ES) barrier favoring the uphill diffusion of atoms allows for a computational reproduction of the experimentally obtained film morphologies.

preprint2011arXiv

Dealloying of Platinum-Aluminum Thin Films Part I. Dynamics of Pattern Formation

Applying focused ion beam (FIB) nanotomography and Rutherford backscattering spectroscopy (RBS) to dealloyed platinum-aluminum thin films an in-depth analysis of the dominating physical mechanisms of porosity formation during the dealloying process is performed. The dynamical porosity formation due to the dissolution of the less noble aluminum in the alloy is treated as result of a reaction-diffusion system. The RBS analysis yields that the porosity formation is mainly caused by a linearly propagating diffusion front, i.e. the liquid/solid interface, with a uniform speed of 42(3) nm/s when using a 4M aqueous NaOH solution at room temperature. The experimentally observed front evolution is captured by the normal diffusive Fisher-Kolmogorov-Petrovskii-Piskounov (FKPP) equation and can be interpreted as a branching random walk phenomenon. The etching front produces a gradual porosity with an enhanced porosity in the surface-near regions of the thin film due to prolonged exposure of the alloy to the alkaline solution.

preprint2011arXiv

Dealloying of Platinum-Aluminum Thin Films Part II. Electrode Performance

Highly porous Pt/Al thin film electrodes on yttria stabilized zirconia electrolytes were prepared by dealloying of co-sputtered Pt/Al films. The oxygen reduction capability of the resulting electrodes was analyzed in a solid oxide fuel cell setup at elevated temperatures. During initial heating to 523 K exceptionally high performances compared to conventional Pt thin film electrodes were measured. This results from the high internal surface area and large three phase boundary length obtained by the dealloying process. Exposure to elevated temperatures of 673 K or 873 K gave rise to degradation of the electrode performance, which was primarily attributed to the oxidation of remaining Al in the thin films.

preprint2011arXiv

Hillock formation of Pt thin films on Yttria stabilized Zirconia single crystals

The stability of a metal thin films on a dielectric substrate is conditioned by the magnitude of the interactive forces at the interface. In the case of a non-reactive interface and weak adhesion, the minimization of free surface energy gives rise to an instability of the thin film. In order to study these effects, Pt thin films with a thickness of 50 nm were deposited via ion-beam sputtering on yttria stabilized zirconia single crystals. All Pt films were subjected to heat treatments up to 973 K for 2 h. The morphological evolution of Pt thin films has been investigated by means of scanning electron microscopy (SEM), atomic force microscopy (AFM) and standard image analysis techniques. Three main observations have been made: i) the deposition method has a direct impact on the morphological evolution of the film during annealing. Instead of hole formation, that is typically observed as response to a thermal treatment, anisotropic pyramidal shaped hillocks are formed on top of the film. ii) It is shown by comparing the hillocks' aspect ratio with finite element method (FEM) simulations that the hillock formation can be assigned to a stress relaxation process inside the thin film. iii) By measuring the equilibrium shapes and the shape fluctuations of the formed Pt hillocks the anisotropy of the step free energy and its stiffness have been derived in addition to the anisotropic kink energy of the hillock's edges.