preprint2010arXiv

Giant magneto-caloric effect near room temperature in Ni-Mn-Sn-Ga alloys

We report the observation of giant magneto-caloric effect (MCE) in ferromagnetic shape memory alloys (FSMAs) of nominal compositions Ni $_2$ Mn $_{1.36}$ Sn $_{0.64-x}$ Ga $_{x}$ ( $x$ =0.24, 0.28 and 0.32). Irrespective of the Ga doping, all the samples undergo long range ferromagnetic ordering below around 330 K. However, the martensitic transition temperature ( $T_{MS}$ ) of the samples varies strongly with Ga concentration. Clear signature of field induced transition around $T_{MS}$ is visible for all the samples. The observed MCE ( $ΔS$ = 13.6 J/kg K for field changing from 0 to 50 kOe) is found to be highest for $x$ = 0.28 with peak near 249 K, while $x$ = 0.32 shows $ΔS$ = 12.8 J/kg K at 274 K. This series of Ga-doped alloys are found to be interesting materials with high value of $ΔS$ over a varied range of temperature

preprint2008arXiv

Reentrant spin glass state in Mn doped Ni2MnSn shape memory alloy

The ground state properties of the ferromagnetic shape memory alloy of nominal composition Ni2Mn1.36Sn0.64 have been studied by dc magnetization and ac susceptibility measurements. Like few other Ni-Mn based alloys, this sample exhibits exchange bias phenomenon. The observed exchange bias pinning was found to originate right from the temperature where a step-like anomaly is present in the zero-field-cooled magnetization data. The ac susceptibility study indicates the onset of spin glass freezing near this step-like anomaly with clear frequency shift. The sample can be identified as a reentrant spin glass with both ferromagnetic and glassy phases coexisting together at low temperature at least in the field-cooled state. The result provides us an comprehensive view to identify the magnetic character of various Ni-Mn-based shape memory alloys with competing magnetic interactions.