Source author record

O. F. Schilling

O. F. Schilling appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.supr-con

Catalog footprint

What is connected

3works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2006arXiv

Experimental observation of two-dimensional fluctuation magnetization in the vicinity of T_c for low values of the magnetic field in deoxygenated YBa_2Cu_3O_{7-x}

We measured isofield magnetization curves as a function of temperature in two single crystal of deoxygenated YBaCuO with T_c = 52 and 41.5 K. Isofield MvsT were obtained for fields running from 0.05 to 4 kOe. The reversible region of the magnetization curves was analyzed in terms of a scaling proposed by Prange, but searching for the best exponent $\upsilon$. The scaling analysis carried out for each data sample set with $\upsilon$=0.669, which corresponds to the 3D-xy exponent, did not produced a collapsing of curves when applied to MvsT curves data obtained for the lowest fields. The resulting analysis for the Y123 crystal with T_c = 41.5 K, shows that lower field curves collapse over the entire reversible region following the Prange's scaling with $\upsilon$=1, suggesting a two-dimensional behavior. It is shown that the same data obeying the Prange's scaling with $\upsilon$=1 for crystal with T_c = 41.5 K, as well low field data for crystal with $T_c$ = 52 K, obey the known two-dimensional scaling law obtained in the lowest-Landau-level approximation.

preprint2004arXiv

Vortex dynamics differences in YBaCuO at low temperatures for H||ab planes due to twin boundary pinning anysotropy

We measured magnetization, M, of a twin-aligned single crystal of YBa2Cu 3Ox (YBaCuO), with Tc = 91 K, as a function of temperature, T, and magnetic field, H, with H applied along the ab planes. Isothermal M-vs.-H and M-vs.-time curves were obtained with H applied parallel and perpendicular to the twin boundary, TB, direction. M-vs.-H curves exhibited two minimums below 38 K, which resembled similar curves that have been obtained in YBaCuO for H parallel to c axis. Above 12 K, the field positions of the minimums for H||TB and HperpTB were quite similar. Below 12 K, the position of the second minimum, Hmin, occurred at a higher field value with H||TB. Below 6 K, only one minimum appeared for both field directions. At low temperatures, these minimums in the M-vs.-H curves produced maximums in the critical current. It was determined that vortex lines were expelled more easily for H||TB than for HperpTB, and, therefore, below a certain field value, that Jc(HperpTB) was larger than Jc(H||TB) . At T<12 K with H||TB, the relaxation rate for flux lines leaving the crystal was found to be different from that for flux entering the crystal. We also observed flux jumps at low temperatures, with their sizes depending on the orientation of magnetic field with respect to the TBs.

preprint2002arXiv

Experimental observation of high field diamagnetic fluctuations in Niobium

We have performed a magnetic study of a bulk metallic sample of Nb with critical temperature $T_{c}=8.5$ K. Magnetization versus temperature (M {\it vs} T) data obtained for fixed magnetic fields above 1 kOe show a superconducting transition which becomes broader as the field is increased. The data are interpreted in terms of the diamagnetic lowest Landau level (LLL) fluctuation theory. The scaling analysis gives values of the superconducting transition temperature $T_{c}(H)$ consistent with $H_{c2}(T)$% . We search for universal 3D LLL behavior by comparing scaling results for Nb and YBaCuO, but obtain no evidence for universality.