The Strain Derivatives of in HgBaCuO: CuO Plane Alone is Not Enough
The strain derivatives of along the and axes have been determined for HgBaCuO (Hg1201), the simplest monolayer cuprate with the highest of all monolayer cuprates ( = 97 K at optimal doping). The underdoped compound with the initial of 65 K has been studied as a function of pressure up to 20 GPa by magnetic susceptibility and X-ray diffraction (XRD). The observed linear increase in with pressure is the same as previously been found for the optimally-doped compound. The above results have enabled the investigation of the origins of the significantly different values of optimally doped Hg1201 and the well-studied compound LaSrCuO (LSCO), the latter value of = 40 K being only about 40% of the former. Hg1201 can have almost identical CuO octahedra as LSCO if specifically strained. When the apical and in-plane CuO distances are the same for the two compounds, a large discrepancy in their remains. Differences in crystal structures and interactions involving the Hg-O charge reservoir layers of Hg1201 may be responsible for the different values exhibited by the two compounds.