BZPEERReading, trust and collaboration for researchDiscover
Workspaces
Network
Opportunities
Account
Researcher profile
M. Yu. Matskevich contributes to research discovery and scholarly infrastructure.
Trust snapshot
Actions
Identity and collaboration
Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.
Log in to claimDirect collaboration
Claim this author entity first to unlock direct invitations.
Research graph
Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.
BZPEER is loading the nearby papers, people, topics and institutions for this page.
Published work
The Bi12.5Nd1.5ReO24.5 tetragonal phase has been synthesized and lattice cell parameters have been determined. According to X-ray data the phase has I4/m sym-metry with lattice parameters a = 0.86742 (12) nm, c =1.7408 (3) nm.
The preparation of BaCeO3 doped by yttrium and indium oxides (BaCe0.6Y0.3In0.1O2.8) has been performed by solid-state reaction from BaCO3, CeO2, Y2O3, In2O3. The compound BaCe0.6Y0.3In0.1O2.8 has been synthesized for the first time. The X-ray measurements have showed that BaCe0.6Y0.3In0.1O2.8 has an orthorhombic structure (space group Pmcn). The standard formation enthalpies of BaCe0.6Y0.3In0.1O2.8 have been determined by solution calorimetry combining the solution enthalpies of BaCe0.6Y0.3In0.1O2.8 and BaCl2 + 0.6CeCl3 + 0.3YCl3 + 0.1InCl3 mixtures in 1 M HCl with 0.1 M KI at 298.15 K and literature data. It has been obtained that above-mentioned mixed oxide is thermodynamically stable with respect to their decomposition into binary oxides at room temperatures. It has been also shown that BaCe0.6Y0.3In0.1O2.8 has been more thermodynamically favored than BaCe0.9In0.1O2.95.
The Bi12.5Sm1.5ReO24.5 phase has been synthesized for the first time. The preparation of Bi12.5Sm1.5ReO24.5 has been performed by solid-state reaction from Bi2O3, Gd2O3, Re2O7. The X-ray measurements have showed that Bi12.5Sm1.5ReO24.5 was cubic structure (space group Fm3m). The standard molar enthalpy of formation of Bi12.5Sm1.5ReO24.5 has been determined by solution calorimetry combining the enthalpies of dissolution of Bi12.5Sm1.5ReO24.5 and 6.25Bi2O3 + 0.75Sm2O3 + 0.5Re2O7 mixture in 2 M HCl and literature data. It has been obtained that above-mentioned phase is thermodynamically stable with respect to their decomposition into binary oxides at room temperatures.
In this paper for the first time we synthesized the compound BaCe0.7Nd0.2In0.1O2.85 by solid-state reaction. The phase has orthorhombic structure (space group Pmcn). We also measured the standard formation enthalpies of BaCe0.7Nd0.2In0.1O2.85 by solution calorimetry in 1 M HCl with 0.1 M KI. We determined the stability of Nd(In)-doped barium cerate with respect to mixtures of binary oxides. On the basis of these data we established that above-mentioned mixed oxide is thermodynamically stable with respect to their decomposition into binary oxides at room temperatures. We also established that BaCe0.7Nd0.2In0.1O2.85 oxide is thermodynamically favoured than BaCe0.8Nd0.2O2.9.