Researcher profile

I. V. Vyazovkin

I. V. Vyazovkin contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

cond-mat.mtrl-sci

Trust snapshot

Quick read

Trust 15 - Baseline

3works

0followers

1topics

4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2016arXiv

Solution enthalpies of barium cerates co-doped by rare-earth elements and indium

The dissolution enthalpies of BaCe0.7Ho0.2In0.1O2.85 and BaCe0.7Sm0.2In0.1O2.85 were measured by method of solution calorimetry in 1M hydrochloric acid with adding 0.1 M KI. The obtained data were compared with earlier measured data on dissolution enthalpies of BaCe0.7Nd0.2In0.1O2.85, BaCe0.7Gd0.2In0.1O2.85. The dependence of dissolution enthalpies from lanthanide radius was constructed. As was shown the relationship is not linear.

preprint2013arXiv

Solution calorimetry investigations of new phase BaCe0.6Y0.3In0.1O2.8

The preparation of BaCeO3 doped by yttrium and indium oxides (BaCe0.6Y0.3In0.1O2.8) has been performed by solid-state reaction from BaCO3, CeO2, Y2O3, In2O3. The compound BaCe0.6Y0.3In0.1O2.8 has been synthesized for the first time. The X-ray measurements have showed that BaCe0.6Y0.3In0.1O2.8 has an orthorhombic structure (space group Pmcn). The standard formation enthalpies of BaCe0.6Y0.3In0.1O2.8 have been determined by solution calorimetry combining the solution enthalpies of BaCe0.6Y0.3In0.1O2.8 and BaCl2 + 0.6CeCl3 + 0.3YCl3 + 0.1InCl3 mixtures in 1 M HCl with 0.1 M KI at 298.15 K and literature data. It has been obtained that above-mentioned mixed oxide is thermodynamically stable with respect to their decomposition into binary oxides at room temperatures. It has been also shown that BaCe0.6Y0.3In0.1O2.8 has been more thermodynamically favored than BaCe0.9In0.1O2.95.

preprint2012arXiv

Formation enthalpy of BaCe0.7Nd0.2In0.1O2.85

In this paper for the first time we synthesized the compound BaCe0.7Nd0.2In0.1O2.85 by solid-state reaction. The phase has orthorhombic structure (space group Pmcn). We also measured the standard formation enthalpies of BaCe0.7Nd0.2In0.1O2.85 by solution calorimetry in 1 M HCl with 0.1 M KI. We determined the stability of Nd(In)-doped barium cerate with respect to mixtures of binary oxides. On the basis of these data we established that above-mentioned mixed oxide is thermodynamically stable with respect to their decomposition into binary oxides at room temperatures. We also established that BaCe0.7Nd0.2In0.1O2.85 oxide is thermodynamically favoured than BaCe0.8Nd0.2O2.9.