Evolution of the pseudogap temperature dependence in YBa$_2$Cu$_3$O$_{7-δ}$ films under the influence of a magnetic field

The evolution of the temperature dependence of pseudogap $Δ$*(T) in optimally doped (OD) YBa$_2$Cu$_3$O$_{7-δ}$ (YBCO) films with $T_{c}$ = 88.7 K under the influence of a magnetic field $B$ up to 8 T has been studied in detail. It has been established that the shape of $Δ$*(T) for various $B$ over the entire range from the pseudogap opening temperature $T$* to $T_{01}$, below which superconducting fluctuations occur, has a wide maximum at the BEC-BCS crossover temperature $T_{pair}$, which is typical for OD films and untwinned YBCO single crystals. $T$* was shown to be independent on $B$, whereas $T_{pair}$ shifts to the low temperature region along with increase of $B$, while the maximum value of $Δ$*($T_{pair}$) remains practically constant regardless of $B$. It was revealed that as the field increases, the low-temperature maximum near the 3D-2D transition temperature $T_{0}$ is blurred and disappears at $B$ > 5 T. Moreover, above the Ginzburg temperature $T_{G}$, which limits superconducting fluctuations from below, at $B$ > 0.5 T, a minimum appears on $Δ$*(T) at $T_{min}$, which becomes very pronounced with a further increase in the field. As a result, the overall value of $Δ$*(T) decreases noticeably most likely due to pair-breaking affect of a magnetic field. A comparison of $Δ$*(T) near $T_{c}$ with the Peters-Bauer theory shows that the density of fluctuating Cooper pairs actually decreases from <<n$_{\uparrow}$n$_{\downarrow}$>> $\approx$ 0.31 at $B$ = 0 to <<n$_{\uparrow}$n$_{\downarrow}$>> $\approx$ 0.28 in the field 8 T. The observed behavior of $Δ$*(T) around $T_{min}$ is assumed to be due to the influence of a two-dimensional vortex lattice created by the magnetic field, which prevents the formation of fluctuating Cooper pairs near $T_{c}$.