Tuning cryogenic Jahn-Teller transition temperatures in magnetoelectric rare earth vanadates
Few materials undergo cooperative Jahn-Teller (JT) transitions at low temperatures, but zircon-type oxides are one class that includes DyVO, which transforms from a tetragonal to an orthorhombic structure at around 13.6 K, with a narrow transition temperature range within 0.5 K. Since many rare-earth ions can be accommodated in the structure, there should be ample routes to vary the transition temperature and structural effects of the transition. We have synthesized pure DyVO and solid solutions DyTmVO ( = 0.05, 0.1, 0.15, 0.2, and 0.5) and DyPrVO ( = 0.03, 0.05, 0.1, 0.2, and 0.5), all by solution precipitation. X-ray diffraction shows a systematic peak shift and a linear change of lattice parameters with increasing substitution. We demonstrate through heat capacity measurements that both Tm and Pr substitutions cause a depression of the cooperative JT transition temperature. When the substitution level increases, the JT transition is eventually suppressed. We examine a mean-field approximation model that can explain the both the JT transition temperature shift and its eventual disappearance. The cooperative JT effect in these zircon-type oxides is known to exhibit a large magnetoelectric response, which should follow from the mean-field behavior. The structural transformation can be easily detected via diffraction and can be used as a temperature calibration in low temperature experiments.