Magnetoelastic anisotropy in Heusler-type MnCoGa films
Perpendicular magnetization is essential for high-density memory application using magnetic materials. High-spin polarization of conduction electrons is also required for realizing large electric signals from spin-dependent transport phenomena. Heusler alloy is a well-known material class showing the half-metallic electronic structure. However, its cubic lattice nature favors in-plane magnetization and thus minimizes the perpendicular magnetic anisotropy (PMA), in general. This study focuses on an inverse-type Heusler alloy, MnCoGa (MCG) with a small off-stoichiometry () , which is expected to be a half-metallic material. We observed relatively large uniaxial magnetocrystalline anisotropy constant () of the order of 10 J/m at room temperature in MCG films with a small tetragonal distortion of a few percent. A positive correlation was confirmed between the ratio of lattice constants and . Imaging of magnetic domains using Kerr microscopy clearly demonstrated a change in the domain patterns along with . X-ray magnetic circular dichroism (XMCD) was employed using synchrotron radiation soft x-ray beam to get insight into the origin for PMA. Negligible angular variation of orbital magnetic moment () evaluated using the XMCD spectra suggested a minor role of the so-called Bruno's term to . Our first principles calculation reasonably explained the small and the positive correlation between the ratio and . The origin of the magnetocrystalline anisotropy was discussed based on the second-order perturbation theory in terms of the spin--orbit coupling, claiming that the mixing of the occupied - and the unoccupied -spin states is responsible for the PMA of the MCG films.