Theoretical study of the stability of the tetradymite-like phases of SbS, BiS, and SbSe
We report a comparative theoretical study of the \textit{Pnma} and \textit{R-3m} phases of SbS, BiS, and SbSe close to ambient pressure. Our enthalpy calculations at 0 K show that at ambient pressure the \textit{R-3m} (tetradymite-like) phase of SbSe is energetically more stable than the \textit{Pnma} phase, contrary to what is observed for SbS and BiS, and irrespective of the exchange-correlation functional employed in the calculations. The result for SbSe is in contradiction to experiments where all three compounds are usually grown in the \textit{Pnma} phase. This result is further confirmed by free-energy calculations taking into account the temperature dependence of the unit-cell volumes and phonon frequencies. Lattice dynamics and elastic tensor calculations further show that both \textit{Pnma} and \textit{R-3m} phases of SbSe are dynamically and mechanically stable at zero applied pressure. Since these results suggest that the formation of the \textit{R-3m} phase for SbSe should be feasible at close to ambient conditions, we provide a theoretical crystal structure and simulated Raman and infrared spectra to help in its identification. We also discuss the results of the two published works that have claimed to have synthesized tetradymite-like SbSe. Finally, the stability of the \textit{R-3m} phase across the three group-15 \textit{AX} sesquichalcogenides is analysed based on their van der Waals gap and X-X in-plane geometry.