Source author record

J. D. Jorgensen

J. D. Jorgensen appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.supr-con

Catalog footprint

What is connected

2works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2006arXiv

Large Ca Isotope Effect in CaC6

We have measured the Ca isotope effect in the newly discovered superconductor CaC6. The isotope effect coefficient is 0.50(7). If one assumes that this material is a conventional electron-phonon coupled superconductor, this result shows that the superconductivity is dominated by coupling of the electrons by Ca phonon modes and that C phonons contribute very little. Thus, in contrast to MgB2, where phonons in the B layers are responsible for the superconductivity, in CaC6 the phonons are primarily modes of the intercalated Ca.

preprint2003arXiv

Crystal Chemistry of Carbon-Substituted MgB2

Neutron powder diffraction has been used to characterize a sample of C-substituted MgB2 synthesized from Mg and B4C (with isotopically enriched 11B). The sample is multiphase, with the major phase [73.4(1) wt.%] being Mg(B1-xCx)2 with x=0.10(2). Minor phases include MgB2C2, Mg, and MgO. The major Mg(B1-xCx)2 phase displays diffraction peak widths as sharp as for pure MgB2, indicating good C homogeneity. There is no evidence for ordering of the substituted C atoms or distortion of the host structure other than contraction of the a axis and slight expansion of the c axis. The observed changes in lattice parameters vs. C concentration provide a means for estimating the C concentration in other Mg(B1-xCx)2 samples. The reduction in Tc resulting from 10% C substitution is much larger than previously reported, suggesting that previous reports of the C concentration in Mg(B1-xCx)2 are overestimated. The Mg site occupancy is determined to be 0.990(4) which is consistent with full Mg occupancy. Given these results, the stoichiometry Mg(B0.9C0.1)2 should be used by future attempts (band structural or otherwise) to explain (i) the dramatic suppression of Tc (Tc ~ = 22 K) and (ii) the persistence of the two-superconducting-gap feature in the specific heat data.