Source author record

Israel Felner

Israel Felner appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.str-el cond-mat.supr-con

Catalog footprint

What is connected

4works

2topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2019arXiv

Magnetic phase diagram of sigma-phase Fe55Re45 compound in the H-T coordinates

In-field DC and AC magnetization measurements were carried out on a sigma-phase Fe55Re45 intermetallic compound aimed at determination of the magnetic phase diagram in the H-T plane. Field cooled, M_FC, and zero-field cooled, M_ZFC, DC magnetization curves were measured in the magnetic field, H, up to 1200 Oe. AC magnetic susceptibility measurements were carried out at a constant frequency of 1465 Hz under DC fields up to H=500 Oe. The obtained results provide evidences for re-entrant magnetism in the investigated sample. The magnetic phase diagrams in the H-T plane have been outlined based on characteristic temperatures determined from the DC and AC measurements. The phase diagrams are similar yet not identical. The main difference is that in the DC diagram constructed there are two cross-over transitions within the strong-irreversibility spin-glass state, whereas in the AC susceptibility based diagram only one transition is observed. The border lines (irreversibility, cross-over) can be described in terms of the power laws.

preprint2013arXiv

Superconductivity and unusual magnetic behavior in amorphous carbon

Traces of superconductivity (SC) at elevated temperatures (up to 65 K) were observed by magnetic measurements in three different inhomogeneous sulfur doped amorphous carbon (a-C) systems: (a) in commercial and (b) synthesized powders and (c) in a-C thin films. (a) Studies performed on commercial (a-C) powder which contains 0.21% of sulfur, revealed traces of non-percolated superconducting phases below Tc = 65 K. The SC volume fraction is enhanced by the sulfur doping. (b) a-C powder obtained by pyrolytic decomposition of sucrose did not show any sign for SC above 5 K. This powder was mixed with sulfur and synthesized at 400 C (a-CS). The inhomogeneous products obtained, show traces of SC phases at TC= 17 and 42 K. (c) Non-superconducting composite a-C-W thin films were grown by electron-beam induced deposition. SC emerged at Tc = 34.4 K only after heat treatment with sulfur. Other parts of the pyrolytic a-CS powder, show unusual magnetic features. (i) Pronounced irreversible peaks around 55-75 K appear in the first zero-field-cooled (ZFC) sweep only. Their origin is not known. (ii) Unexpectedly these peaks are totally suppressed in the second ZFC runs measured a few minutes later. (iii) Around the peak position the field-cooled (FC) curves cross the ZFC plots (ZFC>FC). These peculiar magnetic observations also ascribed to a-CS powder prepared from the commercial a-C powder and are connected to each other. All SC and magnetic phenomena observed are intrinsic properties of the sulfur doped a-C materials. It is proposed that the a-CS systems behave similarly to well known high TC curates and/or pnictides in which SC emerges from magnetic states.

preprint2012arXiv

57Fe Mossbauer spectroscopy and magnetic measurements of oxygen deficient LaFeAsO

We report on the magnetic behavior of oxygen deficient LaFeAsO1-x (x-0.10) compound, prepared by one-step synthesis, which crystallizes in the tetragonal (S.G. P4/nmm) structure at room temperature. Resistivity measurements show a strong anomaly near 150 K, which is ascribed to the spin density wave (SDW) instability. On the other hand, dc magnetization data shows paramagnetic-like features down to 5 K, with an effective moment of 0.83 mB/Fe. 57Fe Mossbauer studies (MS) have been performed at 95 and 200 K. The spectra at both temperatures are composed of two sub-spectra. At 200 K the major one (88%), is almost a singlet, and corresponds to those Fe nuclei, which have two oxygen ions in their close vicinity. The minor one, with a large quadrupole splitting, corresponds to Fe nuclei, which have vacancies in their immediate neighborhood. The spectrum at 95 K, exhibits a broadened magnetic split major (84%) sub-spectrum and a very small magnetic splitting in the minor subspectrum. The relative intensities of the subspectra facilitate in estimating the actual amount of oxygen vacancies in the compound to be 7.0(5)%, instead of the nominal LaFeAsO0.90. These results, when compared with reported 57Fe MS of non-superconducting LaFeAsO and superconducting LaFeAsO0.9F0.1, confirm that the studied LaFeAsO0.93 is a superconductivity-magnetism crossover compound of the newly discovered Fe based superconducting family.

preprint2009arXiv

Magnetization Measurement of a Possible High-Temperature Superconducting State in Amorphous Carbon Doped with Sulfur

Magnetization M(T,H) measurements performed on thoroughly characterized commercial amorphous carbon powder doped with sulfur (AC-S), revealed the occurrence of an inhomogeneous superconductivity (SC) below T_c = 38 K. The constructed magnetic field-temperature (H-T) phase diagram resembles that of type-II superconductors. However, AC-S demonstrates a number of anomalies. In particular, we observed (1) a non-monotonic behavior of the lower critical field H_c1(T); (2) a pronounced positive curvature of the "upper critical field boundary" that we associated with the flux lattice melting line Hm(T); (3) a spontaneous ferromagnetic-like magnetization M0 coexisting with SC. Based on the analysis of experimental results we propose a nonstandard SC state in AC-S.