Researcher profile

Imre Bakonyi

Imre Bakonyi contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

Trust snapshot

Quick read

Trust 17 - UnverifiedVerification L1Unclaimed author
4works
0followers
1topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Identity and collaboration

How to connect with this researcher

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Log in to claim

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

4 published item(s)

preprint2017arXiv

Thermoelectric power factor enhancement by spin-polarized currents - a nanowire case study

Thermoelectric (TE) measurements have been performed on the workhorses of today's data storage devices, exhibiting either the giant or the anisotropic magnetoresistance effect (GMR and AMR). The temperature-dependent (50-300 K) and magnetic field-dependent (up to 1 T) TE power factor (PF) has been determined for several Co-Ni alloy nanowires with varying Co:Ni ratios as well as for Co-Ni/Cu multilayered nanowires with various Cu layer thicknesses, which were all synthesized via a template-assisted electrodeposition process. A systematic investigation of the resistivity, as well as the Seebeck coefficient, is performed for Co-Ni alloy nanowires and Co-Ni/Cu multilayered nanowires. At room temperature, measured values of TE PFs up to 3.6 mWK-2m-1 for AMR samples and 2.0 mWK-2m-1 for GMR nanowires are obtained. Furthermore, the TE PF is found to increase by up to 13.1 % for AMR Co-Ni alloy nanowires and by up to 52 % for GMR Co-Ni/Cu samples in an external applied magnetic field. The magnetic nanowires exhibit TE PFs that are of the same order of magnitude as TE PFs of Bi-Sb-Se-Te based thermoelectric materials and, additionally, give the opportunity to adjust the TE power output to changing loads and hotspots through external magnetic fields.

preprint2016arXiv

Magnetothermopower and magnetoresistance of single Co-Ni/Cu multilayered nanowires

The magnetothermopower and the magnetoresistance of single Co Ni/Cu multilayered nan-owires with various thicknesses of the Cu spacer are investigated. Both kinds of measurement have been performed as a function of temperature (50 K to 325 K) and under applied magnetic fields perpendicular to the nanowire axis, with magnitudes up to 15 % at room temperature. A linear relation between thermopower S and electrical conductivity σ of the nanowires is found, with the magnetic field as an implicit variable. Combining the linear behavior of the S vs. σ and the Mott formula, the energy derivative of the resistivity has been determined. In order to extract the true nanowire materials parameters from the measured thermopower, a simple model based on the Mott formula is employed to distinguish the individual thermopower contributions of the sample. By assuming that the non-diffusive thermopower contributions of the nanowire can be neglected, it was found that the magnetic field induced changes of thermopower and resistivity are equivalent. The emphasis in the present paper is on the comparison of the magnetoresistance and magnetothermopower results and it is found that the same correlation is valid between the two sets of data for all samples, irrespective of the relative importance of the giant magnetoresistance or anisotropic magnetoresistance contributions in the various individual nanowires.

preprint2015arXiv

Modeling the magnetoresistance vs. field curves of GMR multilayers with antiferromagnetic and/or orthogonal coupling by assuming single-domain state and coherent rotation

In order to better understand the role of possible couplings in determining the giant magnetoresistance (GMR) behavior of multilayers, a knowledge of the dependence of the $GMR$ on magnetic field $H$ appears to be useful. Since a few specific cases have only been treated theoretically in the literature, it was decided to carry out a modeling of the $GMR(H)$ curves of ferromagnetic/non-magnetic (FM/NM) multilayers with various interlayer couplings. For simplicity, we focused on a trilayer structure (FM1/NM/FM2) corresponding fairly well to the case of a large number of FM/NM bilayers. To carry out the calculations, some fundamental assumptions were made: (i) single domain FM layer, in plane magnetization; (ii) the magnetization of each layer is the same; (iii) the magnetization vectors rotate in the plane of the layers in an external magnetic field. In order to calculate the $GMR(H)$ function, we need to know the magnetization process in the trilayer, i.e., the $M(H)$ function. Therefore, first we calculate the equilibrium angle $ϕ(H)$ between the two magnetization vectors as a function of the field by minimizing the total energy of the trilayer. According to most previous theoretical and experimental works, the angular dependence of the GMR is fairly well described by the relation $GMR(ϕ)\propto (1-\cosϕ)$ and we used this relation to derive the $GMR(H)$ function. Along this line, the $M(H)$ and $GMR(H)$ curves were calculated for the following cases: (i) pure AF coupling; (ii) pure orthogonal coupling; (iii) AF coupling and orthogonal coupling simultaneously present. As to the calculation of the $GMR(H)$ curves, some of these configurations have not yet been treated formerly or for some specific parameter values only. For those cases for which calculations were reported in the literature for $M(H)$ and $GMR(H)$, our results agree with previous reports.

preprint2014arXiv

Near-substrate composition depth profile of direct current-plated and pulse-plated Fe-Ni alloys

Composition depth profiles of d.c.-plated and pulseplated Fe-Ni alloys have been investigated with the reverse depth profile analysis method. When d.c. plating is applied, the mole fraction of iron near the substrate is higher than during steadystate deposition since iron is preferentially deposited beside nickel and the achievement of the steadystate deposition condition takes time. The steadystate composition was achieved typically after depositing a 90-nm-thick alloy layer. In the pulseplating mode, samples with nearly uniform composition could be obtained at a duty cycle of 0.2 or smaller, and a continuous change in the composition profile could be seen as a function of the duty cycle above this value. A constant sample composition was achieved with pulseplating in a wide peak current density interval. The composition depth profile was also measured for a wide range of Fe2+ concentration. The different characteristics of the composition depth profile as a function of the deposition mode can be explained mostly in terms of mass transport effects. The elucidation of the results is fully in accord with the kinetic models of anomalous codeposition and with the assumption of the superposition of a stationary and a pulsating diffusion layer. The results achieved help to identify the conditions for the deposition of ultrathin magnetic samples with uniform composition along the growth direction.