Correlation of high temperature X-ray photoemission spectral features and conductivity of epitaxially strained (La0.8Sr0.2)0.95Ni0.2Fe0.8O3/SrTiO3(110)
Reversible and irreversible discontinuities at around 573 K and 823 K in the electric conductivity of a strained 175 nm thin film of (La0.8Sr0.2)0.95Ni0.2Fe0.8O3-δ grown by pulsed laser deposition on SrTiO3 (110) are reflected by valence band changes as monitored in photoemission and oxygen K-edge x-ray absorption spectra. The irreversible jump at 823 K is attributed to depletion of doped electron holes and reduction of Fe4+ to Fe3+, as evidenced by oxygen and iron core level soft x-ray spectroscopy, and possibly of a chemical origin, whereas the reversible jump at 573 K possibly originates from structural changes.