Researcher profile

B. F. O. Costa

B. F. O. Costa contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

cond-mat.mtrl-sci cond-mat.str-el

Trust snapshot

Quick read

Trust 15 - UnverifiedVerification L1Unclaimed author

3works

0followers

2topics

3close collaborators

Actions

Decide how to stay connected

Follow researcher0

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2015arXiv

Debye temperature of nanocrystalline Fe-Cr alloys obtained by mechanical alloying

A series on nanocrystalline Fe100-xCrx alloys prepared by mechanical alloying was investigated with X-ray diffraction (XRD), scanning electron microscopy (SEM) and Mössbauer spectroscopy (MS) techniques. XRD and SEM were used to structurally characterize the samples whereas MS permitted phase analysis as well as determination of the Debye temperature, Theta_D. Concerning the latter, an enhancement relative to bulk Theta_D-values was revealed in the range of ca. 40 < x <50. In a sample of Fe55.5Cr44.5 two phases were detected viz. (1) crystalline and magnetic with Theta_D=572(56) K and (2) amorphous and paramagnetic with Theta_D=405(26) K.

preprint2009arXiv

Debye temperature of disordered bcc-Fe-Cr alloys

Debye temperature, TD, of Fe100-xCrx disordered alloys with 0<x<99.9 was determined from the temperature dependence of the centre shift of 57Fe Mossbauer spectra recorded in the temperature range of 80-300K. Its compositional dependence shows an interesting non-monotonous behaviour. For 0<x<~45 as well as for ~75<x<~95 the Debye temperature is enhanced relative to its value of a metallic iron, and at x=~3 there is a local maximum having a relative height of ~12% compared to a pure iron. For ~45<x<~75 and for x>~95 the Debye temperature is smaller than the one for the metallic iron, with a local minimum at x=~55 at which the relative decrease of TD amounts to ~12%. The first maximum coincides quite well with that found for the spin-waves stiffness coefficient, D0, while the pretty steep decrease observed for x>~95 which is indicative of a decoupling of the probe Fe atoms from the underlying chromium matrix is likely related to the spin-density waves which constitute the magnetic structure of chromium in that interval of composition. The harmonic force constant calculated from the Debye temperature of the least Fe-concentrated alloy (x>99.9) amounts to only 23% of the one characteristic of a pure chromium.

preprint2008arXiv

Anomalous behavior of the Debye temperature in Fe-rich Fe-Cr alloys

Debye temperature, $Θ_D$, of Fe-rich Fe$_{100-x}$Cr$_x$ disordered alloys with $0\le x \le 22.3$ was determined from the temperature dependence of the central shift of Mössbauer spectra recorded in the temperature range of 60 -- 300 K. Its compositional dependence shows a maximum at $x \approx 5$ with a relative increase of $\sim 30$% compared to a pure iron. The composition at which the effect occurs correlates well with that at which several other quantities, e. g. the Curie temperature and the spin-wave stiffness coefficient, $D_0$, show their maxima, but the enhancement of $Θ_D$ is significantly greater and comparable with the enhancement of the hyperfine field (spin-density of itinerant $s$-like electrons) in the studied system. The results suggest that the electron-phonon interaction is important in this alloy system.