Source author record

A. M. Pereira

A. M. Pereira appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci cond-mat.str-el

Catalog footprint

What is connected

3works

2topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2016arXiv

Ferroelectric imprint in annealed Bi0.9La0.1Fe0.9Mn0.1O3 thin films

The present work reports the study of the optimized processing conditions of Bi0.9La0.1Fe0.9Mn0.1O3 thin films, grown by RF sputtering on platinum metalized silicon substrates. The combination of deposition at relatively low substrate temperature followed by adequate ex situ annealing leads to thin films with smooth surface morphology and the formation of a high-quality monophasic layer, with the (100)c preferable orientation. The annealed films show ferroelectric imprint.

preprint2015arXiv

Influence of short time milling in R5(Si,Ge)4, R =Gd and Tb, magnetocaloric materials

The effect of the short milling times on R5(Si,Ge)4 R =Gd, Tb magnetocaloric material properties was investigated. In particular, the effect of milling on atomic structure, particles size and morphology, magnetic, and magnetocaloric effect was studied. With short milling times (< 2.5h), a reduction of the Gd5Si1.3Ge2.7 and Tb5Si2Ge2 particles size was achieved down to approximately 3.5 DSm. For both compositions the main differences are a consequence of the milling effect on the coupling of the structural and magnetic transitions. In the Gd5Si1.3Ge2.7 case, a second-order phase transition emerges at high temperatures as a result of ball milling. Consequently, there is a decrease in the magnetocaloric effect of 35% after 150 minutes of milling. Interestingly, an opposite effect is observed in Tb5Si2Ge2 where a 23% increase of the magnetocaloric effect was achieved, driven by the enhancement of the coupling between magnetic and structural transitions arising from internal strain promoted by the milling process.

preprint2010arXiv

Strong magneto-elastic coupling and polar properties in orthorhombic Eu1-xYxMnO3 manganite

This work reports an experimental investigation of the magneto-elastic coupling and polarization character of magnetic phases of the orthorhombic Eu1-xYxMnO3 system at low temperatures. The temperature dependence of the polarization reversal curves clearly reveals the existence of a reentrant improper ferroelectric phase for x = 0.2 and 0.3. Although a ferroelectric phase is also stable for x = 0.4, we have no experimental evidence that it vanishing at finite temperatures. From these results and those obtained from other experimental techniques, the corresponding (x,T) phase diagram was traced, yet yielding significant differences with regard to previous reports. An expressive magneto-elastic coupling is revealed by changes observed in both Mn-O bond lengths and Mn-O1-Mn bond angle at the magnetic phase transitions, obtained by temperature dependence of synchrotron x-ray diffraction experiments. Furthermore, signatures of the lattice deformations across the magnetic phase transitions were evidenced by anomalies in the temperature dependence of the lattice mode involving rotations of the MnO6 octahedra. These anomalies confirm the important role of the spin-phonon coupling in these materials.