Spatially controlled formation of superparamagnetic (Mn,Ga)As nanocrystals in high temperature annealed (Ga,Mn)As/GaAs superlattices

The annealing-induced formation of (Mn,Ga)As nanocrystals in (Ga,Mn)As/GaAs superlattices was studied by X-ray diffraction, transmission electron microscopy and magnetometry. The superlattice structures with 50 A thick (Ga,Mn)As layers separated by 25, 50 and 100 A thick GaAs spacers were grown by molecular beam epitaxy at low temperature (250 C), and then annealed at high temperatures of: 400, 560 and 630 C. The high temperature annealing causes decomposition to GaMnAs ternary alloy and formation of (Mn,Ga)As nanocrystals inside the GaAs matrix. The nanocrystals are confined in the planes that were formerly occupied by (Ga,Mn)As layers for up to the 560 C of annealing and diffuse throughout the GaAs spacer layers at 630 C annealing. The corresponding magnetization measurements show the evolution of the magnetic properties of as-grown and annealed samples from ferromagnetic, through superparamagnetic to the combination of both.