Nanoscale insights on the origin of the Power MOSFETs breakdown after extremely long high temperature reverse bias stress

In this work, the origin of the dielectric breakdown of 4H-SiC power MOSFETs was studied at the nanoscale, analyzing devices that failed after extremely long (three months) of high temperature reverse bias (HTRB) stress. A one-to-one correspondence between the location of the breakdown event and a threading dislocation propagating through the epitaxial layer was found. Scanning probe microscopy (SPM) revealed the conductive nature of the threading dislocation and a local modification of the minority carriers concentration. Basing on these results, the role of the threading dislocation on the failure of 4H-SiC MOSFETs could be clarified.