Abstract
The degree of laser-induced graphitisation from a sp3-bonded to a sp2-bonded carbon fraction in a single crystal chemical vapour deposited (CVD) diamond under a varying fluence of an ultrashort pulsed laser (30 fs, 800 nm, 1 kHz) irradiation has been studied. The tetrahedral CVD sp3-phase was found to transition to primarily an sp2-aromatic crystalline graphitic fraction below the critical fluence of 3.9 J/cm2, above which predominantly an amorphous carbon was formed. A fractional increase of fluence from 3.3 J/cm2 to 3.9 J/cm2 (~ 20 %) resulted in a substantial (~ three-fold) increased depth of the sp2-graphitised areas owing to the non-linear interactions associated with an fs-laser irradiation. Additionally, formation of C=O carbonyl group was observed below the critical threshold fluence; the C=O cleavage occurred gradually with the increase of irradiation fluence of 30 fs laser light. The implications for these findings on enhancement of fs-driven processing of diamond are discussed.
Connections
Explore this paper’s authors, topics and related work.
Building this map preview
BZPEER is loading the nearby papers, people, topics and institutions for this page.
Reviews 0
Write a review
No reviews yet.
Discussion 0
Add a comment
No comments yet.