Enhanced Ferroelectricity and Spin Current Waves in M-Type Barium Hexaferrite

The intrinsic ferroelectricity and related dielectric properties of M-type Barium Hexaferrite (BaFe12O19) with excellent magnetic performance are reported in this paper. A classic electric polarization (P-E) hysteresis loop with full saturation, together with two nonlinear reversal current peaks in the I-V curve and huge change of dielectric constant in the vicinity of Curie temperature, have all demonstrated themselves as sufficient experimental evidences to verify the ferroelectricity of BaFe12O19 ceramics. It holds a large remnant polarization at 108 uC/cm2 and a suitable coercive field at 117 kV/cm. Two peaks at 194C and 451C in the temperature-dependent dielectric spectrum of BaFe12O19 ceramics are considered to be the phase transition from ferro- to antiferro- and antiferro- to para-electric structures. A conventional strong magnetic hysteresis loop was also observed. The magnetically induced polarization upon the BaFe12O19 ceramics was achieved in the form of alternating spin current waves. A ME-coupling voltage with an amplitude of 23mV on an applied magnetic field at 500mT was achieved. These combined multiple functional responses of large ferroelectrics and strong ferromagnetism reveal the excellent multiferroic features of BaFe12O19, which would bring forth the great opportunity to create novel electric devices with active coupling effect between magnetic and electric orders.