Source author record

Y. Katsura

Y. Katsura appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.supr-con

Catalog footprint

What is connected

3works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2013arXiv

Superconductivity at 6 K and the violation of Pauli limit in Ta2PdxS5

Ta2PdxS5 (x < 1.0) was found to show superconductivity at Tc ~ 6 K. The temperature dependent resistivity of single crystalline Ta2Pd0.92S5 showed that the system is strongly disordered due to Pd deficiencies and close to Anderson localized state. Superconductivity in the dirty limit as well as the temperature dependence of specific heat C(T) implies that superconductivity is s-wave. The upper critical field Hc2 at T = 0 K limit with the magnetic field parallel to the TaS6 chains was found to be as high as 31 T, exceeding the Pauli paramagnetic limit Hp = 10.2 T by a factor of 3. We argue that the absence of the paramagnetic pair-breaking originates from strong spin-orbit scattering due to Pd deficiencies embedded in the periodic lattice of heavy 5d Ta and 4d Pd.

preprint2012arXiv

Strong coupling superconductivity at 8.4 K in an antiperovskite phosphide SrPt3P

We report the discovery of a family of ternary platinum phosphides APt3P (A = Ca, Sr and La), which crystallize in an antiperovskite-based structure closely related to that of the heavy fermion superconductor CePt3Si. All three phosphides showed superconductivity at low temperatures and the highest critical temperature Tc = 8.4 K was observed for SrPt3P. The analysis of specific heat C(T) for SrPt3P shows clear evidence for very strong coupling s-wave superconductivity with a large ratio between superconducting gap D0 and Tc, 2D0/kBTc ~ 5, and the presence of low-energy phonons. The presence of multiple Fermi surface pockets was inferred from the nonlinear magnetic field dependence of Hall resistivity, which we argue might play a role in realizing the strong coupling of charge carriers with the low lying phonons.

preprint2010arXiv

Structural Features of Layered Iron Pnictide Oxides (Fe2As2)(Sr4M2O6)

Structural features of newly found perovskite-based iron pnictide oxide system have been systematically studied. Compared to REFePnO system, perovskite-based system tend to have lower Pn-Fe-Pn angle and higher pnictogen height owing to low electronegativity of alkaline earth metal and small repulsive force between pnictogen and oxygen atoms. As-Fe-As angles of (Fe2As2)(Sr4Cr2O6), (Fe2As2)(Sr4V2O6) and (Fe2Pn2)(Sr4MgTiO6) are close to ideal tetrahedron and those pnictogen heights of about 1.40 A are close to NdFeAsO with optimized carrier concentration. These structural features of this system may leads to realization of high Tc superconductivity.