Magnetic and transport properties of tetragonal- or cubic-Heusler-type Co-substituted Mn-Ga epitaxial thin films

The composition dependence of the structural, magnetic, and transport properties of epitaxially grown Mn-Co-Ga films were investigated. The crystal structure was observed to change from tetragonal to cubic as the Co content was increased. In terms of the dependence of saturation magnetization on the Co content, relatively small value was obtained for the Mn $_{2.3}$ Co $_{0.4}$ Ga $_{1.3}$ film at a large {\it K} $_\textrm u$ value of 9.2 Merg/cm $^3$ . Electrical resistivity of Mn-Co-Ga films was larger than that of pure Mn-Ga film. The maximum value of the resistivity was 490 $μΩ$ cm for Mn $_{2.2}$ Co $_{0.6}$ Ga $_{1.2}$ film. The high resistivity of Mn-Co-Ga might be due to the presence of localized electron states in the films due to chemical disordering caused by the Co substitution.

preprint2012arXiv

Perpendicularly magnetized Mn-Co-Ga-based thin films with high coercive field

Mn $_{3-x}$ Co $_{x}$ Ga epitaxial thin films were grown on MgO substrates by magnetron co-sputtering. Structures were tetragonal or cubic depending on Co content. Composition dependence of saturation magnetization and uniaxial magnetic anisotropy $K_u$ of the films were investigated. A high $K_u$ (1.2 MJ m $^{-3}$ ) was achieved for the Mn $_{2.6}$ Co $_{0.3}$ Ga $_{1.1}$ film with the magnetic moment 0.84 $μ_B$ . Valence band spectra were obtained by hard X-ray photoelectron spectroscopy. Sharp peaks in the cubic case, which were absent in the tetragonal case, prove that a van Hove singularity causes a band Jahn-Teller effect with tetragonal distortion. Observations agree well with the first-principles calculations.