Researcher profile

T. Schemme

T. Schemme contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

cond-mat.mtrl-sci

Trust snapshot

Quick read

Trust 15 - Baseline

3works

0followers

1topics

4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2016arXiv

Electronic and magnetic structure of epitaxial NiO/Fe$_3$O$_4$(001) heterostructures grown on MgO(001) and Nb-doped SrTiO$_3$(001)

We study the underlying chemical, electronic and magnetic properties of a number of magnetite based thin films. The main focus is placed onto NiO/Fe$_3$O$_4$(001) bilayers grown on MgO(001) and Nb-SrTiO$_3$(001) substrates. We compare the results with those obtained on pure Fe$_3$O$_4$(001) thin films. It is found that the magnetite layers are oxidized and Fe$^{3+}$ dominates at the surfaces due to maghemite ($γ$-Fe$_2$O$_3$) formation, which decreases with increasing magnetite layer thickness. From a layer thickness of around 20 nm on the cationic distribution is close to that of stoichiometric Fe$_3$O$_4$. At the interface between NiO and Fe$_3$O$_4$ we find the Ni to be in a divalent valence state, with unambiguous spectral features in the Ni 2p core level x-ray photoelectron spectra typical for NiO. The formation of a significant NiFe$_2$O$_4$ interlayer can be excluded by means of XMCD. Magneto optical Kerr effect measurements reveal significant higher coercive fields compared to magnetite thin films grown on MgO(001), and a 45$^{\circ}$ rotated magnetic easy axis. We discuss the spin magnetic moments of the magnetite layers and find that the moment increases with increasing thin film thickness. At low thickness the NiO/Fe$_3$O$_4$ films grown on Nb-SrTiO$_3$ exhibits a significantly decreased spin magnetic moments. A thickness of 20 nm or above leads to spin magnetic moments close to that of bulk magnetite.

preprint2016arXiv

From Fe$_3$O$_4$/NiO bilayers to NiFe$_2$O$_4$-like thin films through Ni interdiffusion

Ferrites with (inverse) spinel structure display a large variety of electronic and magnetic properties making some of them interesting for potential applications in spintronics. We investigate the thermally induced interdiffusion of Ni$^{2+}$ ions out of NiO into Fe$_3$O$_4$ ultrathin films resulting in off-stoichiometric nickelferrite-like thin layers. We synthesized epitaxial Fe$_3$O$_4$/NiO bilayers on Nb-doped SrTiO$_3$(001) substrates by means of reactive molecular beam epitaxy. Subsequently, we performed an annealing cycle comprising three steps at temperatures of 400\,$^{\circ}$C, 600\,$^{\circ}$C, and 800\,$^{\circ}$C under an oxygen background atmosphere. We studied the changes of the chemical and electronic properties as result of each annealing step with help of hard x-ray photoelectron spectroscopy and found a rather homogenous distribution of Ni and Fe cations throughout the entire film after the overall annealing cycle. For one sample we observed a cationic distribution close to that of the spinel ferrite NiFe$_2$O$_4$. Further evidence comes from low energy electron diffraction patterns indicating a spinel type structure at the surface after annealing. Site and element specific hysteresis loops performed by x-ray magnetic circular dichroism uncovered the antiferrimagnetic alignment between the octahedral coordinated Ni$^{2+}$ and Fe$^{3+}$ ions and the Fe$^{3+}$ in tetrahedral coordination. We find a quite low coercive field of 0.02\,T, indicating a rather low defect concentration within the thin ferrite films.

preprint2015arXiv

Link between local iron coordination, Fe 2p XPS core level line shape and Mg segregation into thin magnetite films grown on MgO(001)

A well ordered Fe(001) ultra thin film epitaxially grown on MgO(001) has been oxidized by post deposition annealing in oxygen atmosphere. LEED patterns indicate the formation of magnetite (Fe$_3$O$_4$) after one hour of oxygen exposure. The LEED pattern remains stable despite annealing the sample for further four hours. In contrast X-ray Photoelectron Spectroscopy (XPS) of the Fe $2p$ core levels suggests the formation of an iron oxide comprising mostly of merely trivalent iron. This discrepancy is analyzed and discussed employing charge transfer multiplet calculations for the Fe $2p$ XPS spectra. We find that Mg ion segregation from the substrate into the magnetite thin film replacing octahedrally coordinated Fe$^{2+}$ ions and the excess occupation of octahedral sites which are unoccupied in the ideal inverse spinel structure are driving forces for the altered shape of the Fe $2p$ XPS spectra. Different potential models which might explain the nature of the Mg ion segregation into the magnetite films are discussed.