BZPEERReading, trust and collaboration for research
Menu

Discover

GraphFollow connections around a paper, topic or saved view.

Workspaces

HomePick up where your research flow left off.InboxHandle requests, replies and notifications from one place.CollectionsCurate reading lists, evidence sets and shareable dossiers.ResearchSee your private provenance graph, trail and imports.CollaborationMove from discovery into focused discussion rooms.PublishDraft, preview and publish full-text research articles.

Network

ExpertsFind specialists worth following or asking for help.CommunitiesJoin research circles organized around shared work.PartnersSee external organizations active around the same topics.

Opportunities

ListingsBrowse roles, calls and collaborations with clearer fit signals.

Account

Log inReturn to your reading and collaboration workspace.Create accountStart saving work, following people and joining teams.
Log inCreate account

Researcher profile

Satoshi Watauchi

Satoshi Watauchi contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate
cond-mat.supr-con

Trust snapshot

Quick read

Trust 21 - EmergingVerification L1Unclaimed author
10works
0followers
1topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Identity and collaboration

How to connect with this researcher

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Log in to claim

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

10 published item(s)

preprint2022arXiv

Investigation of superconductivity in Ce-doped (La,Pr)OBiS2 single crystals

Single crystals of Ce-doped (La,Pr)OBiS2 superconductors, multinary rare-earth elements substituted ROBiS2, were successfully grown. The grown crystals typically had a size of 1-2 mm and a plate-like shape with a well-developed c-plane. The c-axis lattice constants of the obtained (La,Ce,Pr)OBiS2 single crystals were approximately 13.6-13.7 A, and the superconducting transition temperature was 1.23-2.18 K. Valence fluctuations of Ce and Pr were detected through X-ray absorption spectroscopy analysis. In contrast to (Ce,Pr)OBiS2 and (La,Ce)OBiS2, the superconducting transition temperature of (La,Ce,Pr)OBiS2 increased with increasing concentrations of the tetravalent state at the R-site.

0 citations0 reviewsNo code linkedOpen access
preprint2020arXiv

Growth and anisotropy evaluation of NbBiCh$_3$ (Ch = S, Se) misfit-layered superconducting single crystals

NbBiCh$_3$ (Ch = S, Se) misfit-layered superconducting single crystals were successfully grown using a CsCl/KCl flux for the first time. The obtained crystals had a well-developed habit parallel to the c-plane with a typical width of 1-2 mm and thickness of 10-40 um. The superconducting transition temperatures with zero resistivity of NbBiS$_3$ single crystals obtained from the nominal composition of Nb0.9Bi1.2S3 was 0.31 K, and that value of the NbBiSe$_3$ single crystals grown from the stoichiometry composition (NbBiSe$_3$) was 2.3 K. Sharp decreases in electric resistivity and magnetic susceptibility at approximately 3 K suggested a possible superconducting transition temperature of NbBiSe$_3$. The normal-state anisotropy values of grown NbBiS$_3$ and NbBiSe$_3$ single crystals were 2.2-2.4 and 1.5-1.6, respectively.

0 citations0 reviewsNo code linkedOpen access
preprint2016arXiv

Superconductivity in CeOBiS2 with cerium valence fluctuation

Resistivities of single-crystalline as well as poly-crystalline samples of CeOBiS2 without fluorine doping were measured at temperatures down to 0.13 K, and were compared with those of poly-crystalline LaOBiS2 and PrOBiS2. Both poly-crystalline and single-crystalline CeOBiS2 exhibited zero resistivity below 1.2 K while poly-crystalline LaOBiS2 and PrOBiS2 did not show zero resistivity down to 0.13 K. Superconducting transition temperature of CeOBiS2 was reduced by increasing the applied current density. The superconductivity of CeOBiS2 without chemical doping is likely triggered by the carriers induced by the valence fluctuation between Ce3+ and Ce4+.

0 citations0 reviewsNo code linkedOpen access
preprint2015arXiv

C-axis electrical resistivity of PrO$_{1-a}$F$_a$BiS$_2$ single crystals

The high anisotropy in RO1-aFaBiS2 (R denotes a rare-earth element) superconductors demonstrates their potential use as intrinsic Josephson junctions, considering the weak coupling among BiS2-PrO(F)-BiS2 (superconducting-normal-superconducting) layers along the c-axis. We grew PrO1-aFaBiS2 single crystals using CsCl/KCl flux. The superconducting anisotropies of the grown single crystals were estimated to be approximately 40-50 from the effective mass model. The c-axis transport properties were characterized using single-crystal s-shaped intrinsic Josephson junctions with a focused ion beam. Along the c-axis, the crystals showed zero resistivity at 2.7 K and a critical current density of 1.33*10^3 A/cm2 at 2.0 K. The current-voltage curve along the c-axis displayed hysteresis. The c-axis transport measurements under a magnetic field parallel to the ab-plane revealed a "lock-in" state due to the Josephson vortex flow, indicating that BiS2 superconductors are promising candidates for intrinsic Josephson junctions.

0 citations0 reviewsNo code linkedOpen access
preprint2014arXiv

Crystal structures of LaO1-xFxBiS2 (x~0.23, 0.46): effect of F doping on distortion of Bi-S plane

The crystal structures of superconducting LaO1-xFxBiS2 (x ~ 0.23, 0.46) were determined by single-crystal X-ray diffraction analysis. Their space group was P4/nmm. Distortion of the Bi-S plane changed when the F content was increased from 0.23 to 0.46, and a nearly flat Bi-S plane was formed at x ~ 0.46. Computational calculations supported this effect of F doping on distortion of Bi-S plane. LaO1-xFxBiS2 with higher F contents were computationally predicted to be thermodynamically more unstable under ambient pressure. We discussed the bonding, conductivities, and synthetic routes of LaO1-xFxBiS2.

0 citations0 reviewsNo code linkedOpen access
preprint2014arXiv

Growth and superconducting anisotropies of F-substituted LaOBiSe2 single crystals

F-substituted LaOBiSe2 single crystals were grown using CsCl flux. The obtained single crystals showed a plate-like shape with a size of about 1.0 mm square. The c-axis lattice constant of the grown crystals was determined to be 14.114(3) Å. The superconducting critical temperature of the single crystal was approximately 3.5 K. The superconducting anisotropies were determined to be 49 and 24 using the upper critical field and the effective mass model, respectively.

0 citations0 reviewsNo code linkedOpen access
preprint2013arXiv

Growth and superconducting properties of F-substituted ROBiS2 (R = La, Ce, Nd) single crystals

F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2 mm in size. The flux components of Cs, K, and Cl were not detected in the obtained single crystals by electron probe microanalysis. The grown single crystals of F-substituted LaOBiS2 and CeOBiS2 showed superconducting at about 3 K while the Tc of the F-substituted NdOBiS2 exhibited approximately 5 K. The superconducting anisotropy of the single crystals of F-substituted LaOBiS2 and NdOBiS2 was estimated to be 30-45 according to the effective mass model whereas those values were 13-21 for the F-substituted CeOBiS2 single crystals. The F-substituted CeOBiS2 single crystals exhibited magnetic order at about 7 K that apparently coexisted with superconductivity below around 3 K.

0 citations0 reviewsNo code linkedOpen access
preprint2013arXiv

Structural Analysis and Superconducting Properties of F-Substituted NdOBiS2 Single Crystals

F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of 1-2 mm and a well-developed ab-plane. The crystal structure of the grown crystals was determined by single-crystal X-ray diffraction analysis to be the tetragonal space group P4/nmm (#129) with a = 3.996(3) A and c = 13.464(6) A. The chemical formula of the grown crystals was approximately Nd0.98(0.06)O0.7(0.1)F0.3(0.1)Bi0.98(0.04)S2, and Cs, K, and Cl were not detected in the grown crystals by electron probe microanalysis. The grown crystals had a critical temperature of approximately 5 K. The superconducting anisotropy of the single crystals was estimated to be about 30 from the effective mass model and the upper critical field.

0 citations0 reviewsNo code linkedOpen access
preprint2010arXiv

Growth and Anisotropic Properties of RBa_2Cu_3O_x Single-Crystal Whiskers

Single-crystal whiskers of RBa2Cu3Ox (R-123, R = Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Y) were successfully grown from Sb- or Te-doped precursors with a nominal composition of R1.5Ba2.75-3.00Cu3M0.5Ox (M: Sb,Te). The whiskers were grown parallel to the ab-plane with the following typical dimensions: 2-8 mm in length, 20-80 \mum in width, and 10-30 \mum in thickness. In the case of rare-earth ions (R3+) with a small ionic radius (Dy, Ho, Er, Tm, Yb, and Y), R-123 whiskers were grown from Te-doped precursors. The growths of Y-123 and Ho-123 whiskers were confirmed using both Te-doped and Sb-doped precursors. On the other hand, for rare-earth ions (R3+) with a large ionic radius (Sm, Eu, and Gd), R-123 whiskers were grown only from Sb-doped precursors. Sb and Te were not detected in the grown whiskers by electron probe microanalysis. The anisotropies of R-123 single-crystal whiskers in the flux liquid state were estimated to be 6.0-33 from the angular dependence of their resistivities under various magnetic fields. The anisotropy increased with decreasing superconducting transition temperature.

0 citations0 reviewsNo code linkedOpen access