BZPEERReading, trust and collaboration for research
Menu

Discover

GraphFollow connections around a paper, topic or saved view.

Workspaces

HomePick up where your research flow left off.InboxHandle requests, replies and notifications from one place.CollectionsCurate reading lists, evidence sets and shareable dossiers.ResearchSee your private provenance graph, trail and imports.CollaborationMove from discovery into focused discussion rooms.PublishDraft, preview and publish full-text research articles.

Network

ExpertsFind specialists worth following or asking for help.CommunitiesJoin research circles organized around shared work.PartnersSee external organizations active around the same topics.

Opportunities

ListingsBrowse roles, calls and collaborations with clearer fit signals.

Account

Log inReturn to your reading and collaboration workspace.Create accountStart saving work, following people and joining teams.
Log inCreate account

Researcher profile

Saleem J. Denholme

Saleem J. Denholme contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate
cond-mat.supr-con

Trust snapshot

Quick read

Trust 21 - EmergingVerification L1Unclaimed author
8works
0followers
1topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Identity and collaboration

How to connect with this researcher

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Log in to claim

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

8 published item(s)

preprint2016arXiv

Origin of the Higher-$T_\rm{c}$ Phase in the K$_x$Fe$_{2-y}$Se$_2$ System

Single crystals of K$_x$Fe$_{2-y}$Se$_2$ are prepared by quenching at various temperatures. The crystals obtained at higher quenching temperatures have a surface morphology with mesh-like texture. They show a sharp superconducting transition at $T_\rm{c}$ ~32 K with a large shielding volume fraction. On the other hand, the crystals prepared without quenching show an onset superconducting transition at ~44 K and a zero resistivity around ~33 K, and they possess island-like regions on the surface with a larger amount of Fe incorporation. In-situ high-temperature single crystal X-ray diffraction measurements tell us the Fe-vacancy ordered phase is generated at a temperature region around 270 °C via iron diffusion. The creation of this Fe-vacancy ordered phase may become a driving force of the growth of the higher $T_\rm{c}$ phase. The superconductivity at ~44 K is attributed to a metallic phase with no Fe-vacancy.

0 citations0 reviewsNo code linkedOpen access
preprint2015arXiv

Electrochemical deposition of FeSe on RABiTS tapes

FeSe film is successfully fabricated onto Rolling Assisted Biaxially Textured Substrate (RABiTS) tapes by an electrochemical deposition technique. The deposited FeSe films tend to become high crystallinity with a decrease in the applied voltage to -1.0 V, and the compositional ratio of Fe to Se approaches 1:1. The sample deposited at -1.0 V shows a superconducting transition approximately 8.0 K in the magnetic susceptibility.

0 citations0 reviewsNo code linkedOpen access
preprint2015arXiv

Site Selectivity on Chalcogen Atoms in Superconducting La(O,F)BiSSe

Single crystals of La(O,F)BiSSe were successfully grown by a CsCl flux method. Single crystal X-ray structural analysis revealed that the crystal structure is isostructural with BiS$_2$- or BiSe$_2$-based compounds with space group $P4/nmm$ (lattice parameters $a$ = 4.1110(2) Å, $c$ = 13.6010(7) Å). However, the S atoms are selectively occupied at the apical site of the Bi-SSe pyramids in the superconducting layer. The single crystals show a superconducting transition at 4.2 K in the magnetic susceptibility and resistivity measurement. The superconducting anisotropic parameter is determined to be 34 from its upper critical magnetic field. The anisotropy is in the same range with that of other members of the La(O,F)BiCh$_2$ ($Ch$ = S, Se) family under ambient pressure.

0 citations0 reviewsNo code linkedOpen access
preprint2014arXiv

First single crystal growth and structural analysis of superconducting layered bismuth oxyselenide; La(O,F)BiSe2

Single crystal of La(O,F)BiSe2 was successfully grown for the first time by the CsCl flux method. Single crystal X-ray structural analysis clearly showed that La(O,F)BiSe2 crystalizes with space group P4/nmm (lattice parameters a = 4.1408(2) Å, c = 14.1096(6) Å). The structure is composed of alternating BiSe2 and LaO layers. Magnetic susceptibility and resistivity measurements showed the superconducting transition at 3.6 K, which is higher than that of as-grown La(O,F)BiS2. The structural analysis implies that La(O,F)BiSe2 is potential superconductor having higher Tc under high pressure.

0 citations0 reviewsNo code linkedOpen access
preprint2014arXiv

High-Tc Phase of PrO0.5F0.5BiS2 single crystal induced by uniaxial pressure

We demonstrated a pressure-induced phase transition from a low-Tc phase (3.5 K) to a high-Tc phase (8.7 K) in single crystalline PrO0.5F0.5BiS2. The high-Tc phase is easily observed even at 0.7 GPa by uniaxial pressure obtained from a geometric effect of a single crystal with an extremely-thin thickness. For this phase transition, superconducting anisotropy and the coherence length along the c axis change from γ = 20 to 9.3 and from ξc = 0.56 to 0.71 nm respectively. It is suggested that a shrinkage in the c lattice constant by applied uniaxial pressure enhances the three dimensionality in the superconducting state.

0 citations0 reviewsNo code linkedOpen access
preprint2014arXiv

Pressure-induced phase transition for single crystalline LaO0.5F0.5BiSe2

We have demonstrated a pressure-induced phase transition from a low-Tc phase to a high-Tc phase in a single crystal of the superconductor LaO0.5F0.5BiSe2. The high-Tc phase appears at 2.16 GPa and the maximum superconducting transition temperature (Tc) is observed at 6.7 K under 2.44 GPa. Although the anisotropy (γ) for the low-Tc phase is estimated to be 20, it is reduced by around half (9.3) in the high-Tc phase. This tendency is the same for the BiS2 system. The Tc of LaO0.5F0.5BiSe2 has continued to increase up to the maximum pressure of this study (2.44 GPa). Therefore applied further pressure has the potential to induce a much higher Tc in this system.

0 citations0 reviewsNo code linkedOpen access
preprint2014arXiv

The effect of exceptionally high fluorine doping on the anisotropy of single crystalline SmFeAsO1-xFx

We succeeded in growing single crystalline SmFeAsO1-xFx with exceptionally high fluorine concentration by using a CsCl flux method. Comparing to conventional flux methods, this method can introduce about double the amount of fluorine into the oxygen site. The obtained single crystal shows the highest superconducting transition temperature (Tc = 57.5 K) in single crystalline iron pnictides. In addition, the residual resistivity ratio (RRR) is almost three times as large as that of previously reported single crystals. This suggests that our single crystals are suitable for investigation of the intrinsic superconducting properties since they have few defects and impurities. Using both the Werthamer-Helfand-Hohenberg model and the effective mass model, we demonstrated that a higher fluorine concentration suppresses the anisotropic superconductivity of SmFeAsO1-xFx.

0 citations0 reviewsNo code linkedOpen access
preprint2013arXiv

Coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2

We show the observation of the coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2(x = 0 - 1.0) prepared by annealing under high-pressure. In CeO1-xFxBiS2 system, both superconductivity and two types of ferromagnetism with respective magnetic transition temperatures of 4.5 K and 7.5 K are induced upon systematic F substitution. This fact suggests that carriers generated by the substitution of O by F are supplied to not only the BiS2 superconducting layers but also the CeO blocking layers. Furthermore, the highest superconducting transition temperature is observed when the ferromagnetism is also enhanced, which implies that superconductivity and ferromagnetism are linked to each other in the CeO1-xFxBiS2 system.

0 citations0 reviewsNo code linkedOpen access