Researcher profile

M. E. Manley

M. E. Manley contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

Trust snapshot

Quick read

Trust 19 - Baseline
5works
0followers
3topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

5 published item(s)

preprint2019arXiv

The Anharmonic Origin of the Giant Thermal Expansion of NaBr

All phonons in a single crystal of NaBr were measured by inelastic neutron scattering at temperatures of 10, 300 and 700 K. Even at 300 K the phonons, especially the longitudinal-optical (LO) phonons, showed large shifts in frequencies, and showed large broadenings in energy owing to anharmonicity. Ab initio computations were first performed with the quasiharmonic approximation (QHA), in which the phonon frequencies depend only on $V$, and on $T$ only insofar as it alters $V$ by thermal expansion. This QHA was an unqualified failure for predicting the temperature dependence of phonon frequencies, even 300 K, and the thermal expansion was in error by a factor of four. Ab initio computations that included both anharmonicity and quasiharmonicity successfully predicted both the temperature dependence of phonons and the large thermal expansion of NaBr. The frequencies of LO phonon modes decrease significantly with temperature owing to the real part of the phonon self-energy from explicit anhamonicity, originating from the cubic anharmonicity of nearest-neighbor Na-Br bonds. Anharmonicity is not a correction to the QHA predictions of thermal expansion and thermal phonon shifts, but dominates the behavior.

preprint2011arXiv

Lattice dynamical origin of peak thermoelectric performance in AgPbmSbTe2+m observed by inelastic neutron scattering

Phonon densities of states (DOS) for the high performing thermoelectric material, AgPbmSbTe2+m (LAST-m, m = 16, 18, and 20), were extracted from time-of-flight inelastic neutron scattering measurements. The phonon DOS of LAST-18 differs remarkably from LAST-16 and LAST-20 by exhibiting a dramatic broadening of its acoustic modes that increases on heating. This broadening coincides with a minimum in the thermal conductivity, a maximum in the electrical conductivity and Seebeck coefficient, and a related peak in thermoelectric performance. We argue that the anomalous broadening originates with scattering enhanced by modifications to Te-Ag(Sb) bonds caused by their resonant electronic states falling near the Fermi energy for m = 18.

preprint2010arXiv

Einstein Modes in the Phonon Density of States of the Single-Filled Skutterudite Yb$_{0.2}$Co$_{4}$Sb$_{12}$

Measurements of the phonon density of states by inelastic neutron \emph{time-of-flight} scattering and specific heat measurements along with first principles calculations, provide compelling evidence for the existence of an Einstein oscillator ("\emph{rattler}") at $ω_{E1} \approx$ 5.0 meV in the filled skutterudite Yb$_{0.2}$Co$_{4}$Sb$_{12}$. Multiple dispersionless modes in the measured density of states of Yb$_{0.2}$Co$_{4}$Sb$_{12}$ at intermediate transfer energies (14 meV $\leq$ \emph{$ω$} $\leq$ 20 meV) are exhibited in both the experimental and theoretical \emph{density-of-states} of the Yb-filled specimen. A peak at 12.4 meV is shown to coincide with a second Einstein mode at \emph{$ω_{E2} \approx$} 12.8 meV obtained from heat capacity data. The local modes at intermediate transfer energies are attributed to altered properties of the host CoSb$_{3}$ cage as a result of Yb-filling. It is suggested that these modes are owed to a complementary mechanism for the scattering of heat-carrying phonons in addition to the mode observed at $ω_{E1} \, \approx$ 5.0 meV. Our observations offer a plausible explanation for the significantly-higher \textit{dimensionless figures of merit} of filled skutterudites, compared to their parent compounds.

preprint2010arXiv

Impact of intrinsic localized modes of atomic motion on materials properties

Recent neutron and x-ray scattering measurements show intrinsic localized modes (ILMs) in metallic uranium and ionic sodium iodide. Here, the role ILMs play in the behavior of these materials is examined. With the thermal activation of ILMs, thermal expansion is enhanced, made more anisotropic, and, at a microscopic level, becomes inhomogeneous. Interstitial diffusion, ionic conductivity, the annealing rate of radiation damage, and void growth are all influenced by ILMs. The lattice thermal conductivity is suppressed above the ILM activation temperature while no impact is observed in the electrical conductivity. This complement of transport properties suggests that ILMs could improve thermoelectric performance. Ramifications also include thermal ratcheting, a transition from brittle to ductile fracture, and possibly a phase transformation in uranium.

preprint2006arXiv

Valence-Band UPS, 6$p$ Core-Level XPS Photoemission Spectroscopy, and Low-Energy Electron Diffraction of a Uranium (001) Single Crystal

Valence-band ultraviolet photoemission spectroscopy (UPS) at 173K and 6p core-level X-ray photoemission spectroscopy (XPS) at room temperature were performed on a high quality uranium single crystal. Significant agreement is found with first-principles electronic band-structure calculations, using a generalized gradient approximation (GGA). In addition, using Low Energy Electron Diffraction (LEED) for the (001) surface, we find a well-ordered orthorhombic crystallographic structure representative of the bulk material.