From solid solution to cluster formation of Fe and Cr in $α$-Zr
To understand the mechanisms by which Fe and Cr additions increase the corrosion rate of irradiated Zr alloys, a combination of experimental (atom probe tomography, x-ray diffraction and thermoelectric power measurements) and modelling (density functional theory) techniques are employed to investigate the non-equilibrium solubility and clustering of Fe and Cr in binary Zr alloys. Cr occupies both interstitial and substitutional sites in the α-Zr lattice, Fe favours interstitial sites, and a low-symmetry site that was not previously modelled is found to be the most favourable for Fe. Lattice expansion as a function of alloying concentration (in the dilute regime) is strongly anisotropic for Fe additions, expanding the $c$-axis while contracting the $a$-axis. Defect clusters are observed at higher solution concentrations, which induce a smaller amount of lattice strain compared to the dilute defects. In the presence of a Zr vacancy, all two-atom clusters are more soluble than individual point defects and as many as four Fe or three Cr atoms could be accommodated in a single Zr vacancy. The Zr vacancy is critical for the increased solubility of defect clusters, the implications for irradiation induced microstructure changes in Zr alloys are discussed.