Researcher profile

Kazumasa Togano

Kazumasa Togano contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

cond-mat.supr-con

Trust snapshot

Quick read

Trust 21 - Emerging

6works

0followers

1topics

4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2014arXiv

High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

The recently discovered iron-based superconductors with very high upper critical field and small anisotropy have been regarded as a potential candidate material for high field applications. However, enhancements of superconducting properties are still needed to boost the successful use of iron-based superconductors in such applications. Here, we propose a new sheath architecture of stainless steel (SS)/Ag double sheath and investigate its influence on the microstructures and Jc-H property. We found that the transport Jc-H curves for rolled and pressed tapes both show extremely small magnetic field dependence and exceed 3*10^4A/cm^2 under 28 T, which are much higher than those of low-temperature superconductors. More interestingly, 12 cm long rolled tape shows very high homogeneity and sustains Jc as high as 7.7*10^4 A/cm^2 at 10 T. These are the highest values reported so far for iron-based superconducting wires fabricated by scalable rolling process. The microstructure investigations indicate that such high Jc was achieved by higher density of the core and uniform deformation resulting better texturing. These results indicate that our process is very promising for fabricating long Ba122 wires for high field magnet, i.e. above 20 T.

preprint2013arXiv

Achievement of practical level critical current densities in PIT Ba1-xKxFe2As2/Ag tapes by conventional cold mechanical deformation

We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4 T, which is almost the practical level of 105 A/cm2. The Jc-H curve shows extremely small magnetic field dependence and keeps a high value of 6.9x104 A/cm2 in 10 T. These are the highest values reported so far for iron based superconducting wires. We also show our successful attempts of the fabrication of multi-filamentary tapes. A high Jc value of 5.3x104 A/cm2 (4.2 K, 10 T) was obtained in seven-filamentary tapes. The hardness and microstructure investigations reveal that the superior Jc in uniaxial pressed tape samples is due to the high core density, more textured grains and the change of microcrack structure. These results indicate that iron based superconductors are promising for high magnetic field applications.

preprint2013arXiv

Large enhancement of transport critical current density of ex-situ PIT Ag/(Ba,K)Fe2As2 tapes achieved by applying cycles of cold deformation and heat treatment

We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The process involves cycles of the cold deformation and subsequent heat treatment. The intermediate cycles of flat rolling and heat treatment produce uniform fine-grained structure, resulting in an enhancement of transport Jc in applied magnetic fields. However, the rolled tapes contain cracks running traverse to the tape axis, which still limit the current pass along the tape axis. We found that the application of uniaxial pressing with small reduction rate at the final stage is very effective to heal those cracks, resulting in an extraordinary increase of the transport Jc. We achieved the highest Jc (at 4.2 K and 10 T) of 2.1x104 A/cm2 among the PIT processed Fe based wires and tapes reported so far. The Jc-H curves measured at higher temperatures maintains a small filed dependence up to around 20 K, suggesting that the tapes are promising for applications at higher temperatures as well as in liquid helium.

preprint2011arXiv

A New Noncentrosymmetric Superconducting Phase in the Li-Rh-B System

Superconductivity, at 2-3 K, was observed in a novel phase of the ternary Li-Rh-B system. The structural phase exhibits a large noncentrosymmetric cubic unit cell with the a-parameter being within 1.208 \leq a \leq 1.215 nm. This phase is stable over a wider compositional range of LixRhBy (0.6 < x < 2, 1 < y < 2). The superconductivity, as well as the unit cell volume, is sensitive to the Li/B content but it is manifested with Tc \geq 1.8 K over a wider compositional range: the highest Tc \approx 3 K occurs for x : y \approx 0.9:1.5 with a \approx 1.209 nm. The superconducting shielding fraction of most samples is almost 80% of that of Sn. The lower critical field, Hc1(0), is ~65 Oe while the upper one, Hc2(0) is determined from extrapolation to be higher than 14 kOe. We discuss the influence of pressure on Tc and also the influence of the lack of inversion symmetry on the superconducting properties.

preprint2011arXiv

Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process

We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor bulk material prepared by a melting process was ground into powder and put into a Ag tube. The composite was then cold worked into a wire and heat treated at 850$^\circ$C for sintering. Transport critical current densities, Jc, at 4.2 K are 1.0\times104 A/cm2 (Ic = 60.7 A) in self field and 1.1\times103 A/cm2 (Ic = 6.6 A) in 10 T. These are the highest values reported so far for the Fe-based superconducting wires.

preprint2004arXiv

Superconducting Properties of Combustion Synthesized MgB2

We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned to the P6/mmm MgB2 phase. The temperature dependence of magnetization shows sharp superconducting transition around 38K. The critical current density can be estimated from the hysteresis of the magnetization curvature using the Bean's model. The powdered sample shows a high critical current density of 2x10^6 A/cm2 at 5K under the magnetic field of 1T.