Source author record

Jinho An

Jinho An appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci

Catalog footprint

What is connected

3works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2010arXiv

Domain (Grain) Boundaries and Evidence of Twin Like Structures in CVD Grown Graphene

Understanding and engineering the domain boundaries in chemically vapor deposited (CVD) monolayer graphene will be critical for improving its properties. In this study, a combination of transmission electron microscopy (TEM) techniques including selected area electron diffraction (SAED), high resolution transmission electron microscopy (HRTEM), and dark field (DF) TEM was used to study the boundary orientation angle distribution and the nature of the carbon bonds at the domain boundaries. This report provides an important first step towards a fundamental understanding of these domain boundaries. The results show that, for the graphene grown in this study, the 46 measured misorientation angles are all between 11-30 degrees (with the exception of one at 7 degrees). HRTEM images show the presence of adsorbates in almost all of the boundary areas. When a boundary was imaged, defects were seen (dangling bonds) at the boundaries that likely contribute to adsorbates binding at these boundaries. DFTEM images also showed the presence of a 'twin like' boundary.

preprint2010arXiv

Graphene films with large domain size by a two-step chemical vapor deposition process

The fundamental properties of graphene are making it an attractive material for a wide variety of applications. Various techniques have been developed to produce graphene and recently we discovered the synthesis of large area graphene by chemical vapor deposition (CVD) of methane on Cu foils. We also showed that graphene growth on Cu is a surface-mediated process and the films were polycrystalline with domains having an area of tens of square microns. In this paper we report on the effect of growth parameters such as temperature, and methane flow rate and partial pressure on the growth rate, domain size, and surface coverage of graphene as determined by Raman spectroscopy, and transmission and scanning electron microscopy. Based on the results, we developed a two-step CVD process to synthesize graphene films with domains having an area of hundreds of square microns. Scanning electron microscopy and Raman spectroscopy clearly show an increase in domain size by changing the growth parameters. Transmission electron microscopy further shows that the domains are crystallographically rotated with respect to each other with a range of angles from about 13 degrees to nearly 30 degrees. Electrical transport measurements performed on back-gated FETs show that overall films with larger domains tend to have higher carrier mobility, up to about 16,000 cm2 V-1 s-1 at room temperature.

preprint2009arXiv

Large-Area Synthesis of High-Quality and Uniform Graphene Films on Copper Foils

Graphene has been attracting great interest because of its distinctive band structure and physical properties. Today, graphene is limited to small sizes because it is produced mostly by exfoliating graphite. We grew large-area graphene films of the order of centimeters on copper substrates by chemical vapor deposition using methane. The films are predominantly single layer graphene with a small percentage (less than 5%) of the area having few layers, and are continuous across copper surface steps and grain boundaries. The low solubility of carbon in copper appears to help make this growth process self-limiting. We also developed graphene film transfer processes to arbitrary substrates, and dual-gated field-effect transistors fabricated on Si/SiO2 substrates showed electron mobilities as high as 4050 cm2V-1s-1 at room temperature.