BZPEERPapers, people, evidence and research paths
Menu

Discover

SearchFind papers, people, topics, institutions and opportunities from one place.GraphSee how papers, authors, topics and evidence connect.

Research tools

HomeContinue from the papers, people and topics that matter now.CollectionsTurn saved papers into reading lists, evidence maps and shareable context.ResearchReconstruct the path that led you from search to paper to question.CollaborationMove from a paper, topic or expert request into a focused thread.PublishCreate full-text research articles with metadata, formulas and versions.

Network

ExpertsFind specialists whose work and reviews explain why they can help.CommunitiesJoin research groups organized around papers, topics and shared evidence.

Opportunities

ListingsBrowse roles, calls and collaborations connected to real research context.

Account

Log inReturn to your saved papers, graph views and active threads.Create accountStart saving papers, building a research trail and joining teams.
Log inCreate account

Source author record

Jean-Marc Bonard

Jean-Marc Bonard appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record
cond-mat.mtrl-sci

Catalog footprint

What is connected

6works
1topics
4close collaborators

Actions

Connect this record

Log in to claim
Open graphBrowse works

Research graph

See the researcher in context

Open full explorer

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

6 published item(s)

preprint2013arXiv

Influence of the deposition conditions on the field emission properties of patterned nitrogenated carbon nanotube films

The electron field emission of patterned films of nitrogenated carbon nanotubes is shown to be decisively influenced by the deposition conditions. The growth was carried out by decomposing methane in a nitrogen/ammonia atmosphere using hot filament chemical vapor deposition (CVD). The diameter of the produced tubes depended critically on the distance between substrate and filament, and the field emission properties applied fields needed for electron emission, field amplification factor) could be directly correlated to the film morphology. This demonstrates the possibility of tuning the field emission properties of such film emitters. For arrays of nanotubes thinner than 50 nm, the onset of field emission was observed at about 4 V/um, and a current density of 10 mA/cm2 was obtained for an applied field of 7.2 V/um.

0 citations0 reviewsNo code linkedOpen access
preprint2013arXiv

Tailoring the diameter of decorated CN nanotubes by temperature variations using HF-CVD

Patterned films of decorated nitrogenated carbon (C-N) nanotubes were catalytically synthesised by hot filament chemical vapour deposition (HF-CVD) in a nitrogen-methane-ammonia environment. The systematic study of a transition between different kinds of C-N nanostructures as a function of the local substrate temperature ranging from 700 up to 820C is presented. The morphology, the diameter as well as the properties of the generated tubular structures showed strong dependence on this parameter. By means of electron microscopy a new type of decoration covering all tubular structures was observed. Buckled lattice fringes revealed the disordered graphitic-like character of the hollow C-N nanotubes. Raman spectroscopy confirmed a transition in the microscopic order as a function of temperature. Furthermore field emission in vacuum was studied and showed a spectacular correlation to the deposition temperature and therefore the diameter of the C-N tubes. For arrays of tubes thinner than 50 nm an onset field below 4 V/um was observed.

0 citations0 reviewsNo code linkedOpen access
preprint2005arXiv

Comparative study of the catalytic growth of patterned carbon nanotube films

Three different catalysts (Fe, Ni, Co nitrates dissolved in ethanol) were patterned on a SiO2/Si substrate and multi-wall carbon nanotubes were grown by catalytic decomposition of acetylene. We compare the growth of the carbon nanostructures in the temperature range between 580C and 1000C. With our experimental set-up the catalyst solutions of cobalt and nickel were found to be less efficient than the one of iron. An optimal production of multi-wall nanotubes was observed at temperatures between 650C and 720C with the iron solution as catalyst. We found a tendency towards thicker structures with higher temperatures. Finally, we suggest a mechanism for the growth of these carbon structures.

0 citations0 reviewsNo code linkedOpen access
preprint2005arXiv

Formation of metallic nano-crystals from gel-like precursor films for CVD nanotube growth: An in-situ TEM characterization

The evolution of a continuous Fe(NO3)3 catalyst film was observed by in-situ annealing in a Transmission Electron Microscope (TEM). Such catalysts are routinely used in the catalytic growth of carbon nanotubes. The experiments reveal that crystalline particles form from the gel-like film already around 300C. At usual carbon nanotube growth temperatures of 700C, the particles are single-crystalline with a log-normal size distribution. The observations furthermore show that in spite of the crystalline structure of the particles there is a high mobility. The experiments allow to obtain detailed information about the chemistry and the crystallinity of the catalyst film, which provides valuable information for the interpretation of the carbon nanotube growth by chemical vapor deposition.

0 citations0 reviewsNo code linkedOpen access
preprint2005arXiv

Raman spectroscopy and field emission measurements on catalytically grown carbon nanotubes

We used microcontact printing to pattern a silicon surface with an iron-containing catalytic solution. Multi-wall carbon nanotubes were subsequently grown on the patterned areas by chemical vapor deposition at temperatures between 650 and 1000C. We demonstrate that the diameter of the catalytically grown multi-wall nanotubes increases with the deposition temperature. Raman spectroscopy has been used to investigate the crystalline character of the obtained structures and it is found that the fraction of the nano-crystalline shell increases with the temperatures. The measurement of the field emission properties shows a correlation between the tube diameter and the emission field values.

0 citations0 reviewsNo code linkedOpen access
preprint2005arXiv

Thermodynamic calculations on the catalytic growth of multiwall carbon nanotubes

We have developed a thermodynamic model of the catalytic growth of multiwall carbon nanotubes from hydrocarbon precursors at elevated temperature. Using this model we have computed the heat distribution, and carbon concentration in the catalyst. Calculations delivered a analytical formula for the growth time and growth rate. We find that the growth is mainly driven by a concentration gradient within the catalyst, rather than a temperature gradient.

0 citations0 reviewsNo code linkedOpen access