Researcher profile

J. B. Claridge

J. B. Claridge contributes to research discovery and scholarly infrastructure.

ResearcherAffiliation not importedOpen to collaborate

Trust snapshot

Quick read

Trust 17 - UnverifiedVerification L1Unclaimed author
4works
0followers
2topics
4close collaborators

Actions

Decide how to stay connected

Follow researcher0

Identity and collaboration

How to connect with this researcher

Claiming links this public author record to a researcher profile and unlocks direct collaboration workflows.

Log in to claim

Direct collaboration

Open a focused conversation when the fit is right

Claim this author entity first to unlock direct invitations.

Research graph

See the researcher in context

Open full explorer

Inspect adjacent work, topics, institutions and collaborators without jumping out to a separate graph page.

Building this graph slice

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

4 published item(s)

preprint2014arXiv

Growth and characterization of heteroepitaxial La-substituted BaSnO$_3$ films on SrTiO$_3$ (001) and SmScO$_3$ (110) substrates

Heteroepitaxial growth of BaSnO$_3$ (BSO) and Ba$_{1-x}$La$_x$SnO$_3$ (x = 7 %) (LBSO) thin films on different perovskite single crystal (SrTiO$_3$ (001) and SmScO$_3$ (110)) substrates has been achieved by Pulsed Laser Deposition (PLD) under optimized deposition conditions. X-ray diffraction measurements indicate that the films on either of these substrates are relaxed due to the large mismatch and present a high degree of crystallinity with narrow rocking curves and smooth surface morphology while analytical quantification by proton induced x-ray emission (PIXE) confirms the stoichiometric La transfer from a polyphasic target, producing films with La contents above the bulk solubility limit. The films show degenerate semiconducting behavior on both substrates, with the observed room temperature resistivities, Hall mobilities and carrier concentrations of 4.4 $m Ωcm$, 10.11 $cm^2 V^{-1} s^{-1}$, and 1.38 $\cdot 10^{20} cm^{-3}$ on SmScO$_3$ and 7.8 $m Ωcm$, 5.8 $cm^2 V^{-1} s^{-1}$, and 1.36 $\cdot 10^{20} cm^{-3}$ on SrTiO$_3$ ruling out any extrinsic contribution from the substrate. The superior electrical properties observed on the SmScO3 substrate are attributed to reduction in dislocation density from the lower lattice mismatch.

preprint2013arXiv

Engineered spatial inversion symmetry breaking in an oxide heterostructure built from isosymmetric room-temperature magnetically ordered components

The oxide heterostructure [(YFeO$_3$)$_5$(LaFeO$_3$)$_5$]$_{40}$, which is magnetically ordered and piezoelectric at room temperature, has been constructed from two weak ferromagnetic AFeO$_3$ perovskites with different A cations using RHEED-monitored pulsed laser deposition. The polarisation arises through the removal of inversion centres present within the individual AFeO$_3$ components. This symmetry reduction is a result of combining ordering on the A site, imposed by the periodicity of the grown structure, with appropriate orientations of the octahedral tilting characteristic of the perovskite units themselves, according to simple symmetry-controlled rules. The polarisation is robust against A site interdiffusion between the two layers which produces a sinusoidally modulated occupancy that retains the coupling of translational and point symmetries required to produce a polar structure. Magnetization and magneto-optical Kerr rotation measurements show that the heterostructure's magnetic structure is similar to that of the individual components. Evidence of the polarity was obtained from second harmonic generation and piezoelectric force microscopy measurements. Modeling of the piezoresponse allows extraction of $d_{33}$ (approximately 10 pC/N) of the heterostructure, which is in agreement with DFT calculations.

preprint2011arXiv

Cation vacancy order in the K0.8+xFe1.6-ySe2 system: five-fold cell expansion accommodates 20% tetrahedral vacancies

Ordering of the tetrahedral site vacancies in two crystals of refined compositions K0.93(1)Fe1.52(1)Se2 and K0.862(3)Fe1.563(4)Se2 produces a fivefold expansion of the parent ThCr2Si2 unit cell in the ab plane which can accommodate 20% vacancies on a single site within the square FeSe layer. The iron charge state is maintained close to +2 by coupling of the level of alkali metal and iron vacancies, producing a potential doping mechanism which can operate at both average and local structure levels.