Source author record

Harry J Blythe

Harry J Blythe appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci

Catalog footprint

What is connected

3works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2013arXiv

Contrasting behavior of the structural and magnetic properties in Mn- and Fe-doped In$_2$O$_3$ films

We have observed room temperature ferromagnetism (FM) in In$_2$O$_3$ thin films doped with either 5 at.% Mn or Fe, prepared by pulsed laser deposition (PLD) at substrate temperatures ranging from 300 to 600$\,^{\circ}{\rm C}$. The dependence of saturation magnetization on grain size was investigated for both types of In$_2$O$_3$ films. It is revealed that, for the Mn-doped films, the magnetization was largest with small grains, indicating the importance of grain boundaries. In contrast, for Fe-doped films, the largest magnetization was observed with large grains.

preprint2013arXiv

Grain boundary ferromagnetism in vanadium-doped In$_2$O$_3$ thin films

Room temperature ferromagnetism was observed in In$_2$O$_3 thin films doped with 5 at.% vanadium, prepared by pulsed laser deposition at substrate temperatures ranging from 300 to 600 $\,^{\circ}{\rm C}$. X-ray absorption fine structure measurement indicated that vanadium was substitutionally dissolved in the In$_2$O$_3$ host lattice, thus excluding the existence of secondary phases of vanadium compounds. Magnetic measurements based on SQUID magnetometry and magnetic circular dichroism confirm that the magnetism is at grain boundaries and also in the grains. The overall magnetization originates from the competing effects between grains and grain boundaries.

preprint2009arXiv

Magneto-optical properties of Co/ZnO multilayer films

Multilayer films of ZnO with Co were deposited on glass substrates then annealed in a vacuum. The magnetisation of the films increased with annealing but not the magnitude of the magneto-optical signals. The dielectric functions for the films were calculated using the MCD spectra. A Maxwell Garnett theory of a metallic Co/ZnO mixture is presented. The extent to which this explains the MCD spectra taken on the films is discussed.