Source author record

Hanns-Peter Liermann

Hanns-Peter Liermann appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

Catalog footprint

What is connected

4works
3topics
4close collaborators

Actions

Connect this record

Log in to claim

Research graph

See the researcher in context

Open full explorer

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

Published work

4 published item(s)

preprint2019arXiv

High-pressure synthesis of ultraincompressible hard rhenium nitride pernitride Re$_{2}$(N$_{2}$)N$_{2}$ stable at ambient conditions

Here we report the synthesis of metallic, ultraincompressible (bulk modulus $K_{0}$ = 428(10) GPa) and very hard (nanoindentation hardness 36.7(8) GPa) rhenium (V) nitride pernitride Re$_{2}$(N$_{2}$)N$_{2}$. While the empirical chemical formula of the compound, ReN$_{2}$, is the same as for other known transition metals pernitrides, e.g. IrN$_{2}$, PtN$_{2}$, PdN$_{2}$ and OsN$_{2}$, its crystal chemistry is unique. The known pernitrides of transition metals consist of a metal in the oxidation state +IV and pernitride anions N$_{2}^{4-}$. ReN$_{2}$ contains both pernitride N$_{2}^{4-}$ and discrete N$^{3-}$ anions, which explains its exceptional properties. Moreover, in the original experimental synthesis of Re$_{2}$(N$_{2}$)N$_{2}$ performed in a laser-heated diamond anvil cell via a direct reaction between rhenium and nitrogen at pressures from 40 to 90 GPa we observed that the material was recoverable at ambient conditions. Consequently, we developed a route to scale up its synthesis through a reaction between rhenium and ammonium azide, NH$_{4}$N$_{3}$, in a large-volume press at 33 GPa. Our work resulted not only in a discovery of a novel material with unusual crystal chemistry and a set of properties attractive for potential applications, but also demonstrated a feasibility of surmounting conceptions common in material sciences.

preprint2015arXiv

One-dimensional chain "melting" in incommensurate potassium

Between 19 and 54 GPa, potassium has a complex composite incommensurate host-guest structure which undergoes two intraphase transitions over this pressure range. The temperature dependence of these host-guest phases is further complicated by the onset of an order-disorder transition in their guest chains. Here, we report single crystal, quasi-single crystal, and powder synchrotron X-ray diffraction measurements of this order-disorder phenomenon in incommensurate potassium to 47 GPa and 750 K. The so-called chain "melting" transition is clearly visible over a 22 GPa pressure range, and there are significant changes in the slope of the phase boundary which divides the ordered and disordered phases, one of which results from the intraphase transitions in the guest structure.

preprint2015arXiv

Pressure, stress, and strain distribution in the double-stage diamond anvil cell

Double stage diamond anvil cells (DAC) of two designs have been assembled and tested. We used a standard symmetric DAC as a primary stage and CVD microanvils machined by a focused ion beam - as a second. We evaluated pressure, stress, and strain distributions in Au and Fe-Au samples as well as in secondary anvils using synchrotron x-ray diffraction with a micro-focused beam. A maximum pressure of 240 GPa was reached independent of the first stage anvil culet size. We found that the stress field generated by the second stage anvils is typical of conventional DAC experiments. The maximum pressures reached are limited by strains developing in the secondary anvil and by cupping of the first stage diamond anvil in the presented experimental designs. Also, our experiments show that pressures of several megabars may be reached without sacrificing the first stage diamond anvils.

preprint2015arXiv

Residual stress induced stabilization of martensite phase and its effect on the magneto-structural transition in Mn rich Ni-Mn-In/Ga magnetic shape memory alloys

The irreversibility of the martensite transition in magnetic shape memory alloys (MSMAs) with respect to external magnetic field is one of the biggest challenges that limits their application as giant caloric materials. This transition is a magneto-structural transition that is accompanied with a steep drop in magnetization (i.e., 'delta M') around the martensite start temperature (Ms) due to the lower magnetization of the martensite phase. In this communication, we show that 'delta M' around Ms in Mn rich Ni-Mn based MSMAs gets suppressed by two orders of magnitude in crushed powders due to the stabilization of the martensite phase at temperatures well above the Ms and the austenite finish (Af) temperatures due to residual stresses. Analysis of the intensities and the FWHM of the x-ray powder diffraction patterns reveals stabilized martensite phase fractions as 97, 75 and 90% with corresponding residual microstrains as 5.4, 5.6 and 3% in crushed powders of the three different Mn rich Ni-Mn alloys, namely, Mn1.8Ni1.8In0.4, Mn1.75Ni1.25Ga and Mn1.9Ni1.1Ga, respectively. Even after annealing at 773 K, the residual stress stabilised martensite phase does not fully revert to the equilibrium cubic austenite phase as the magneto-structural transition is only partially restored with reduced value of 'delta M'. Our results have very significant bearing on application of such alloys as inverse magnetocaloric and barocaloric materials.