Source author record

Daniel P. Abraham

Daniel P. Abraham appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci

Catalog footprint

What is connected

3works

1topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2015arXiv

Stress Evolution in Lithium-ion Composite Electrodes during Electrochemical Cycling and Resulting Internal Pressures on the Cell Casing

Composite cathode coatings made of a high energy density layered oxide (Li1.2Ni0.15Mn0.55Co0.1O2, theoretical capacity ~377 mAh/g), polyvinylidene fluoride (PVdF) binder, and electron-conduction additives, were bonded to an elastic substrate. An electrochemical cell, built by pairing the cathode with a capacity-matched graphite anode, was electrochemically cycled and the real-time average stress evolution in the cathode coating was measured using a substrate-curvature technique. Features in the stress evolution profile showed correlations with phase changes in the oxide, thus yielding data complementary to in situ XRD studies on this material. The stress evolution showed a complex variation with lithium concentration suggesting that the volume changes associated with phase transformations in the oxide are not monotonically varying functions of lithium concentration. The peak tensile stress in the cathode during oxide delithiation was approximately 1.5 MPa and the peak compressive stress during oxide lithiation was about 6 MPa. Stress evolution in the anode coating was also measured separately using the same technique. The measured stresses are used to estimate the internal pressures that develop in a cylindrical lithium-ion cell with jelly-roll electrodes.

preprint2013arXiv

Stress Evolution in Composite Silicon Electrodes during Lithiation/Delithiation

We report real-time average stress measurements on composite silicon electrodes made with two different binders [Carboxymethyl cellulose (CMC), and polyvinylidene fluoride (PVDF)] during electrochemical lithiation and delithiation. During galvanostatic lithiation at very slow rates, the stress in a CMC-based electrode becomes compressive and increases to 70 MPa, where it reaches a plateau and increases slowly thereafter with capacity. The PVDF-based electrode exhibits similar behavior, although with lower peak compressive stress of about 12 MPa. These initial experiments indicate that the stress evolution in a Si composite electrode depends strongly on the mechanical properties of the binder. Stress data obtained from a series of lithiation/delithiation cycles suggests plasticity induced irreversible shape changes in contacting Si particles, and as a result, the stress response of the system during any given lithiation/delithiation cycle depends on the cycling history of the electrode. While these results constitute the first in-situ stress measurements on composite Si electrodes during electrochemical cycling, the diagnostic technique described herein can be used to assess the mechanical response of a composite electrode made with other active material/binder combinations.

preprint2012arXiv

Real-Time Stress Measurements in Lithium-ion Battery Negative-electrodes

Real-time stress evolution in a graphite-based lithium-ion battery negative-electrode during electrolyte wetting and electrochemical cycling is measured through wafer-curvature method. Upon electrolyte addition, the composite electrode rapidly develops compressive stress of the order of 1-2 MPa due to binder swelling; upon continued exposure, the stress continues to evolve towards an apparent plateau. During electrochemical intercalation at a slow rate, the compressive stress increases with the electrode's state-of-charge, reaching a maximum value of 10 - 12 MPa. There appears to be an approximate correlation between the rate of stress rise and the staging behavior of the lithiated graphite. De-intercalation at a slow rate results in a similar linear decrease in electrode stress. Tensile stress of a few MPa develops at the end of deintercalation in the first few cycles, after which the electrode remains under compressive stress only. Although higher peak stresses are seen at high C-rates, the dependence appears to be relatively weak (up to 5C). These measurements reveal, for the first time, the nature of stress evolution in practical lithium-ion-battery electrodes and provide useful data to quantify the driving force for mechanical damage that accrues in composite electrodes upon repeated cycling. While the reported results can serve as reference for calibrating theoretical and computational models to predict electrode stress and damage evolution, the methodology demonstrated can be used to measure stresses and characterize fatigue damage in any composite lithium-ion-battery electrode as well as optimize its microstructure to mitigate stress-related damage mechanisms.