Source author record

Costantino Creton

Costantino Creton appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.soft cond-mat.mtrl-sci physics.chem-ph

Catalog footprint

What is connected

7works

3topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2021arXiv

3D Fluorescent Mapping of Invisible Molecular Damage after Cavi-tation in Hydrogen Exposed Elastomers

Elastomers saturated with gas at high pressure suffer from cavity nucleation, inflation, and deflation upon rapid or explosive de-compression. Although this process often results in undetectable changes in appearance, it causes internal damage, hampers func-tionality (e.g., permeability), and shortens lifetime. Here, we tag a model poly(ethyl acrylate) elastomer with π-extended anthracene-maleimide adducts that fluoresce upon polymer chain scission, and map in 3D the internal damage present after a cycle of gas satu-ration and rapid decompression. Interestingly, we observe that each cavity observable during the decompression results in a dam-aged region, the shape of which reveals a fracture locus of randomly oriented penny-shape cracks (i.e., with a flower-like morpholo-gy) that contain crack arrest lines. Thus, cavity growth likely proceeds discontinuously (i.e., non-steadily) through the stable and unstable fracture of numerous 2D crack planes. This non-destructive methodology to visualize in 3D molecular damage in polymer networks is novel and serves to understand how fracture occurs under complex 3D loads, predict mechanical aging of pristine look-ing elastomers, and holds potential to optimize cavitation-resistant materials.

preprint2020arXiv

Quantifying and mapping covalent bond scission during elastomer fracture

Many new soft but tough rubbery materials have been recently discovered and new applications such as flexible prosthetics, stretchable electrodes or soft robotics continuously emerge. Yet, a credible multi-scale quantitative picture of damage and fracture of these materials has still not emerged, due to our fundamental inability to disentangle the irreversible scission of chemical bonds along the fracture path from dissipation by internal molecular friction. Here, by coupling new fluorogenic mechanochemistry with quantitative confocal microscopy mapping, we uncover how many and where covalent bonds are broken as an elastomer fractures. Our measurements reveal that bond scission near the crack plane can be delocalized over up to hundreds of micrometers and increase by a factor of 100 depending on temperature and stretch rate, pointing to an intricated coupling between strain rate dependent viscous dissipation and strain dependent irreversible network scission. These findings paint an entirely novel picture of fracture in soft materials, where energy dissipated by covalent bond scission accounts for a much larger fraction of the total fracture energy than previously believed. Our results pioneer the sensitive, quantitative and spatially-resolved detection of bond scission to assess material damage in a variety of soft materials and their applications.

preprint2016arXiv

Fracture of dual crosslink gels with permanent and transient crosslinks

We have carried out systematic fracture experiments in a single edge notch geometry over a range of stretch rates on dual crosslink hydrogels made from polyvinyl alcohol chains chemically crosslinked with glutaraldehyde and physically crosslinked with borate ions. If the energy release rate necessary for crack propagation was calculated conventionally, by using the work done to deform the sample to the critical value of stretch $λ_c$ where the crack propagates, we found that the fracture energy $Γ$ peaks around $λ\sim 0.001 s^{-1}$ before decreasing sharply with increasing stretch rate, in contradiction with the measurements of crack velocity. Combining simulations and experimental observations, we propose therefore here a general method to separate the energy dissipated during loading before crack propagation, from that which is dissipated during crack propagation. For fast loading rates (with a characteristic strain rate only slightly lower than the inverse of the typical breaking time of physical bonds), this improved method to estimate a local energy release rate $g_{local}$ at the onset of crack propagation, gives a value of the local fracture energy $Γ_{local}$ which is constant, consistent with the constant value of the crack propagation velocity measured experimentally. Using this improved method we also obtain the very interesting result that the dual crosslink gels have a much higher value of fracture energy at low loading rates than at high loading rates, contrary to the situation in classical chemically crosslinked elastic networks.

preprint2015arXiv

Rate-dependent elastic hysteresis during the peeling of Pressure Sensitive Adhesives

The modelling of the adherence energy during peeling of Pressure Sensitive Adhesives (PSA) has received much attention since the 1950's, uncovering several factors that aim at explaining their high adherence on most substrates, such as the softness and strong viscoelastic behaviour of the adhesive, the low thickness of the adhesive layer and its confinement by a rigid backing. The more recent investigation of adhesives by probe-tack methods also revealed the importance of cavitation and stringing mechanisms during debonding, underlining the influence of large deformations and of the related non-linear response of the material, which also intervenes during peeling. Although a global modelling of the complex coupling of all these ingredients remains a formidable issue, we report here some key experiments and modelling arguments that should constitute an important step forward. We first measure a non-trivial dependence of the adherence energy on the loading geometry, namely through the influence of the peeling angle, which is found to be separable from the peeling velocity dependence. This is the first time to our knowledge that such adherence energy dependence on the peeling angle is systematically investigated and unambiguously demonstrated. Secondly, we reveal an independent strong influence of the large strain rheology of the adhesives on the adherence energy. We complete both measurements with a microscopic investigation of the debonding region. We discuss existing modellings in light of these measurements and of recent soft material mechanics arguments, to show that the adherence energy during peeling of PSA should not be associated to the propagation of an interfacial stress singularity. The relevant deformation mechanisms are actually located over the whole adhesive thickness, and the adherence energy during peeling of PSA should rather be associated to the energy loss by viscous friction and by rate-dependent elastic hysteresis.

preprint2013arXiv

Quantitative analysis of the debonding structure of soft adhesives

We experimentally investigate the growth dynamics of cavities nucleating during the first stages of debonding of three different model adhesives. The material properties of these adhesives range from a more liquid-like material to a soft viscoelastic solid and are carefully characterized by small strain oscillatory shear rheology as well as large strain uniaxial extension. The debonding experiments are performed on a probe tack set-up. Using high contrast images of the debonding process and precise image analysis tools we quantify the total projected area of the cavities, the average cavity shape and growth rate and link these observations to the material properties. These measurements are then used to access corrected effective stress and strain curves that can be directly compared to the results from the uniaxial extension.

preprint2010arXiv

Self-assembly in solution of a reversible comb-shaped supramolecular polymer

We report a single step synthesis of a polyisobutene with a bis-urea moiety in the middle of the chain. In low polarity solvents, this polymer self-assembles by hydrogen bonding to form a combshaped polymer with a central hydrogen bonded backbone and polyisobutene arms. The comb backbone can be reversibly broken, and consequently, its length can be tuned by changing the solvent, the concentration or the temperature. Moreover, we have proved that the bulkiness of the side-chains have a strong influence on both the self-assembly pattern and the length of the backbone. Finally, the density of arms can be reduced, by simply mixing with a low molar mass bis-urea.

preprint2004arXiv

Cavity Growth in Soft Solids

Soft polymer-based solid materials can be defined as solid materials with elastic moduli below 1 MPa. In order to obtain such a low modulus while retaining a solid character, all these materials are based on a network of fixed points (crosslinks, physical interactions) keeping together a liquid-like matrix. Since they are not able to flow, very large deformations will lead to failure by fracture or cavitation. We discuss in this paper new experimental data suggesting that the growth of a cavity in a soft nearly elastic solid undergoes a transition from a stress-controlled growth, when the initial cavity size is larger than Gc/E, to an energy-activated growth, when the initial cavity size is smaller than Gc/E. The important material length scale Gc/E represents the ratio between the surface energy necessary to expand the cavity and the elastic modulus. This energy activated growth regime is due to the existence of a metastable solution and significantly increases the apparent cavitation stress for layers thinner than 1000 Gc/E.