Source author record

Anton Geiler

Anton Geiler appears in the imported research catalog. Authorship, coauthor and topic links are available while profile ownership is still unclaimed.

ResearcherUnclaimed source record

cond-mat.mtrl-sci cond-mat.mes-hall physics.chem-ph

Catalog footprint

What is connected

3works

3topics

4close collaborators

Actions

Connect this record

Open graph Browse works

Inspect adjacent papers, topics, institutions and collaborators without losing the researcher page.

Building this map preview

BZPEER is loading the nearby papers, people, topics and institutions for this page.

preprint2011arXiv

Magneto-Electric Effects on Sr Z-type Hexaferrite at Room Temperature

In this paper, magnetoelectric effects of Sr Z-type hexaferrite, Sr3Fe24Co2O41, at room temperature is measured. The change in remanence magnetization was measured by applying a DC voltage or electric field across a slab of hexaferrite. Changes of ~ 18% in remanence was observed in an electric field of 10,000V/cm implying a similar change in the microwave permeability at frequencies below 3GHz. Also, a change in dielectric constant at 1 GHz of ~16% in a magnetic field of only 320 Oe was measured. In these types of measurements high resistivity is critical in order to reduce current flow in the hexaferrite. The resistivity of the hexaferrite was raised to 4.28x10^8 ohm-cm by annealing under oxygen pressure. The measurements indicate that indeed electric polarization and magnetization changes were induced by the application of magnetic and electric fields, respectively. The implications for microwave applications appear to be very promising at room temperature.

preprint2011arXiv

Room Temperature Magnetoelectric Effects on Single Slabs of Z-type Hexaferrites

In this paper, magnetoelectric effects of Sr Z-type hexaferrite, Sr3Fe24Co2O41, at room temperature is measured. The change in remanence magnetization was measured by applying a DC voltage or electric field across a slab of hexaferrite. Changes of ~ 18% in remanence was observed in an electric field of 10,000V/cm implying a similar change in the microwave permeability at frequencies below 3GHz. In these types of measurements high resistivity is critical in order to reduce current flow in the hexaferrite. The resistivity of the hexaferrite was raised to 4.28x10^8 ohm?-cm by annealing under oxygen pressure. The measurements indicate that indeed electric polarization and magnetization changes were induced by the application of magnetic and electric fields, respectively. The implications for microwave applications appear to be very promising at room temperature.

preprint2009arXiv

High coercivity cobalt carbide nanoparticles processed via polyol reaction: A new permanent magnet material

Cobalt carbide nanoparticles were processed using polyol reduction chemistry that offers high product yields in a cost effective single-step process. Particles are shown to be acicular in morphology and typically assembled as clusters with room temperature coercivities greater than 4 kOe and maximum energy products greater than 20 KJ/m3. Consisting of Co3C and Co2C phases, the ratio of phase volume, particle size, and particle morphology all play important roles in determining permanent magnet properties. Further, the acicular particle shape provides an enhancement to the coercivity via dipolar anisotropy energy as well as offering potential for particle alignment in nanocomposite cores. While Curie temperatures are near 510K at temperatures approaching 700 K the carbide powders experience an irreversible dissociation to metallic cobalt and carbon thus limiting operational temperatures to near room temperature.